Diffusion bonding titanium to stainless steel using NbCuNi multi-interlayer精选.pdf

M A T E R I A L S C H A R A C T E R I Z A T I O N 6 8 ( 2 0 1 2 ) 8 2 – 8 7 A v a i l a b l e o n l i n e a t w w w . s c i e n c e d i r e c t . c o m w w w . e l s e v i e r . c o m / l o c a t e / m a t c h a r Diffusion bonding titanium to stainless steel using Nb/Cu/Ni multi-interlayer a, b b,⁎ b b b Peng Li , Jinglong Li , Jiangtao Xiong , Fusheng Zhang , Syed Hamid Raza aState Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xian 710072, PR China bShaanxi Key Laboratory of Friction Welding Technologies, Northwestern Polytechnical University, Xian 710072, PR China A R T I C L E D A T A A B S T R A C T Article history: By using Nb/Cu/Ni structure as multi-interlayer, diffusion bonding titanium to austenitic Received 19 November 2011 stainless steel has been conducted. The effects of bonding temperature and bonding time Received in revised form on the interfacial microstructure were analyzed by scanning electron microscope equipped 25 March 2012 with energy dispersive spectroscope, and the joint strength was evaluated by tensile test. Accepted 30 March 2012 The results showed that Ni atoms aggregated at the Cu–Nb interface, which promoted Cu solution in Nb. This phenomenon forms a Cu–Nb solution strengthening effect. However, Keywords: such effect would decay by using long bo