压下量和冷却方式对低碳钢组织和硬度的影响本科综合实验报告.docx

内蒙古科技大学本科生综合实验报告题目：压下量和冷却方式对低碳钢组织和硬度的影响学院：材料与冶金学院专业：材料成型及控制工程姓名：王金铭班级：成型2班学号：1161105204指导老师：郭瑞华老师目 录实验目的········································3实验材料········································3实验方案········································3实验设备及器材··································3金相切割机·································3加热炉（箱式炉）····························3二辊可逆式试验轧机·························3实验步骤········································4试样准备和切割镶嵌·························4加热·······································4轧制·······································4磨样、抛光·································4腐蚀与拍照·································5显微硬度测定·······························5实验结果分析····································6观察和分析Q235不同压下量，不同冷却方式的金相组织·····································6分析造成金相组织不同的原因·················7分析不同冷却速度对硬度的影响···············8实验误差分析·······························8总结············································9参考文献········································9一、实验目的1．通过实验室二辊可逆轧机对Q235钢进行轧制实验，分析其在相同加热温度、轧制温度、压下量的条件下，冷却方式对材料组织的影响。2.认识和熟练使用实验中的各种仪器。3培养学生实践和自主能力。二、实验材料本实验材料所用试样为低合金钢Q235，其主要成分见表1。表1 Q235化学成分 质量分数%牌号 CMn Si S PQ235 0.12~0.22 0.30~0.60 ≤0.30 ≤0.04 ≤0.04三、实验方案把试样Q235放入加热炉中加热，当炉温达到1000℃时，保温20分钟，在取出试样前调整好二辊可逆式实验轧机。保温完成后取出试样在轧机中进行轧制，压下量分别为10%和28%，轧制完成后分别水冷和空冷至室温。冷却后将试样切割，打磨，抛光，腐蚀。然后把经过一系列处理之后的试样放在金相显微镜下观察，如果有清晰的组织就可以进行拍照标注。四、实验设备及器材 1.金相切割机QG-2金相试样切割机（以下简称切割机）是利用高速旋转的薄片砂轮来截取金相试样，它广泛地适用于金相实验室切割各种金属材料。由于本机附有冷却装置，用来带走切割时所产生的热量，因而避免了试样遇热而改变其金相组织。2.加热炉（箱式炉）主要供金属机件或合金钢机件在空气中进行热处理加工之用。与控制柜配合使用，可手动或自动控制电炉的温度。箱式电阻炉结构主要由炉体、炉衬、炉底板、加热元件、炉门及控制系统等部分组成。3.二辊可逆式实验轧机二辊轧机分为可逆式和不可逆式，现在一般都是采用可逆式。二辊轧机主要是通过两个旋转的轧辊将轧件咬入轧机，实现来料尺寸的变化完成轧钢的。轧制板材时轧辊工作面是平面，通过压下装置调节辊缝大小来实现板材厚度的变化。五、实验步骤1.试样准备和切割镶嵌将准备的试样切割，后用镶嵌机镶嵌成成品。2.加热（1）将加热炉手动控制，预设炉内温度为1000℃。（2）将加热炉设置成自动控制进行加热。（3）安排两人随时观察加热炉，保证电流不超过25A，若有异常则立即关闭加热炉，改为手动控制，电流正常以后再改为自动控制。（4）当炉温达到预设温度并保温完成后，取出试样在轧机上进行轧制。（5）轧制完成后，轧件空冷。3.轧制表2 Q235轧制参数试样编号试样代号及厚度尺寸（mm）轧制温度轧制道次道次压下率冷却方 式轧前 厚度轧后厚度1号9.668.721000℃110%水冷2号9.666.951000℃28%空冷4.磨样、抛光（1）将冷却后的试样用切