【论文】掺合料在再生砂浆中的试验研究推荐.docxVIP

掺合料在再生砂浆中的试验研究 李正鹏（云南农业大学水利学院，昆明650201）摘 要目前我国对再生砂浆的研究还属于探索阶段，很多方面都还很不成熟。本文所探究的是掺合料在再生砂浆中的作用，而本文所说的掺合料包括粉煤灰、硅粉、聚丙烯纤维。当聚丙烯纤维一定时探究粉煤灰（10%、20%、30%/40%）、硅粉（10%、20%、30%、40%、60%、80%）聚丙烯纤维定量（1.2k|m3）进行实验。实验表明：掺入粉煤灰能够减弱砂浆的抗压、抗折强度；硅粉能明显的提高天然再生砂浆的抗压抗折强度；当聚丙烯纤维定量1.2k|m3硅粉、粉煤灰变量时，砂浆抗压抗折有最优值；聚丙烯对砂浆的影响是呈曲线的。当聚丙烯纤维、粉煤灰一定量时，硅粉的不同掺量会影响砂浆的抗压、抗折强度。同时当聚丙烯纤维、硅粉一定量时，掺入不同量的粉煤灰也会影响砂浆的抗折、抗压强度。Abstract Our current research is also part of the regeneration of mortar exploratory stage, many aspects still immature. This paper is to explore the mortar admixtures role in regeneration, and this article said admixtures include fly ash, silica fume, polypropylene fibers. When a polypropylene fiber when the inquiry ash (10%, 20%, 30% / 40%), silica fume (10%, 20%, 30%, 40%, 60%, 80%) polypropylene fiber quantification (1.2k | m3) experiment. Experimental results show that: the incorporation of fly ash can be reduced compressive and flexural strength of mortar; silica fume can significantly improve the natural regeneration of mortar compressive and flexural strength; When polypropylene fiber quantitative 1.2k | m3 silica fume, fly ash when variables mortar compressive and flexural have optimal value; impact polypropylene mortar is presented curve. When polypropylene fiber, a certain amount of fly ash, silica fume content will affect different compressive and flexural strength mortar. When the same fiber, a certain amount of silica fume, fly ash is incorporated will affect the amount of different mortar flexural and compressive strength.目录第一章 绪 论1 1-1 引言1 1-2 再生细骨料国内的研究现状1 1-3 再生细骨料的国外研究现状3 1-4主要研究的内容及意义4第二章 材料的基本性能5 2-1-1掺合料的基本性能5 2-1-2细骨料的吸水率7 2-1-3细骨料的堆积密度8 2-1-4细骨料的压碎指标92-2 天然细骨料的基本性质实验 10 2-2-1天然细骨料的表观密度10 2-2-2天然细骨料的堆积密度11 2-2-3天然细骨料的压碎指标12 2-2-4天然细骨料的吸水率实验13 2-2-5天然细骨料的针状、片状含量14 2-2-6天然细骨料的级配试验162-3再生细骨料的基本性能试验17 2-3-1再生细骨料的来源17 2-3-2 再生细骨料的制备过程17 2-3-3再生细骨料的堆积密度19 2-3-4 再生细骨料的表观密度21 2-3-5再生细骨料的压碎指标22 2-3-6 再生细骨料的吸水率试验24 2-3-7 再生细骨料的级配试验24本章小结27第三章 岩浆配合比设计29 3-1初步配合比的计算29 3-2试拌调整，得出基准配合比31 3-3成