中国科技论文在线 电阻点焊电动机支架断裂失效分析 王亚婷，徐越兰，刘敏，李文健* （南京理工大学材料科学与工程系，南京 210094） 摘要：对电阻点焊电动机支架高频振动破坏试样进行了失效分析。通过焊材成分分析、断口 形貌分析和微观金相组织分析，结果表明固定电动机支架发生断裂的原因是由于焊接工艺不 当所致。因此在焊接过程中应该适当改变焊接工艺参数，调整焊接规范。 关键词：电阻点焊；断裂；断口形貌；金相组织 中图分类号：TG405 Failure Analysis of Resistance Spot Welding Motor Bracket Wang Yating, Xu Yuelan, Liu Min, Li Wenjian (Department of Materials Science and Engineering，Nanjing University of Science and Technology,NanJing 210094) Abstract: In this paper failure analysis was made on resistance spot welding motor bracket test specimens who were destroyed by the high-frequency vibration. Welding component analysis, macro-morphology inspection analysis and microscopic analysis of the microstructure show that the reason why the fixed motor bracket was broken was due to improper welding. Therefore, during the welding process the welding parameters should be changed appropriately, and the welding conditions should be adjusted too. Keywords:resistance spot welding;break;macro-morphology inspection;metallographic structure 0 引言 随着航空航天、电子、汽车、家用电器等工业的发展，电阻焊越加受到广泛的重视。同 时，对电阻焊的质量也提出了更高的要求[1] 。然而，目前还缺乏可靠的无损检测方法，焊接 质量只能靠工艺试样和工件的破坏性试验来检查。本文针对具有普遍性的电阻点焊连接中出 现的断裂现象进行分析。 电阻点焊（如图1）的优点是成本低，操作简单，易于实现机械化和自动化，缺点是对 气密性要求不高，容易出现气孔，电流过低时容易产生未焊透的现象，电流过大时容易造成 材料脆性断裂[2] 。 本文所用的破坏性试验方法是高频振动试验，其目的在于确定所设计、制造的机器、构 件在运输和使用过程中承受外来振动或者自身产生的振动而不至破坏，并发挥其性能、达到 预定寿命的可靠性。试验通过对类似结构（螺母和板材连接）进行高频振动达到支架断裂（如 图2 ），并对断裂原因进行说明分析。 作者简介：王亚婷，女，(1986-)，硕士研究生，主要研究方向是焊接冶金与焊接工艺研究. E-mail: wangyating86@163.com - 1 - 中国科技论文在线 断裂处 图1 电阻点焊示意图 图2 支架断裂示意图 1 试验过程 本文所用的材料是Q235 钢，