3_welding_tianjin university_LNG储罐用9Ni钢焊接温度场的数值模拟.pdf

9Ni 钢焊接温度场的数值模拟 1 1,2 1 2 2 李午申 ，白世武 ,严春妍 ，尹长华 ，黄福祥 (1.天津大学材料科学与工程学院，天津 300072 ；2.中国石油天然气管道科学研究院，河北 廊坊 065000) 摘要：采用SYSWELD有限元计算软件，对9Ni钢多道多层焊的焊接温度场进行了数值模拟 ，并实现了焊接材料逐步填 充的模拟，计算结果与试验结果非常一致。利用一次回归正交试验，研究焊接热输入和层间温度对焊接热影响区的热循 环的影响。结果表明，焊后冷却时间t8/3和高温停留时间tH 随着焊接热输入和层间温度的增加而增大。焊接热输入对t8/3 和tH 的影响较为显著，根据焊接生产实际条件 ，应采用小的焊接热输入。 关键词：9Ni 钢；温度场 ；数值模拟 ；焊接工艺参数 中图分类号：TG44 文献标识码：A Numerical Simulation of Temperature Field for 9Ni steel welding LI Wu-shen (School of Materials Science and Engineering, Tianjin University, Tianjin 300072, China) Abstract: Temperature field for 9Ni steel multi-layer welding was simulated using SYSWELD software. Welding material was deposited step by step during this simulation. Linear regression orthogonal experiment was used to investigate the influences of heat input and inter-layer temperature on heat cycles in heat affected zone. Results showed that cooling time t8/3 and dwelling time tH increased with heat input and inter-layer temperature. The effect of heat input influencing t8/3 and tH was more obvious. Small heat input is recommended for 9Ni steel field welding. Key words: 9Ni steel; temperature field; numerical simulation; welding parameters 焊的焊接温度场进行了动态模拟，为焊接工艺参数 0 前言 的合理选择和优化提供了有效的参考依据。 焊接是一个牵涉到传热学、电磁学、材料冶金 1 数学模型的建立 学、固体和流体力学等多学科交叉的复杂过程，焊 接温度场的准确计算是定量计算焊接冶金、焊接应 1.1 温度场计算模型 力应变分析和焊接过程自动化控制的前提。焊接过 在焊接过程中，随着热源的移动，焊件上的温 程的传热问题十分复杂，焊接温度场中各点温度变 度场随时间和空间剧烈变化，同时还存在熔化和相 化率很大，且影响因素繁多，采用传统的实验方法 变时的潜热