原创力文档- 1、原创力文档（book118）网站文档一经付费（服务费），不意味着购买了该文档的版权，仅供个人/单位学习、研究之用，不得用于商业用途，未经授权，严禁复制、发行、汇编、翻译或者网络传播等，侵权必究。。
- 2、本站所有内容均由合作方或网友上传，本站不对文档的完整性、权威性及其观点立场正确性做任何保证或承诺！文档内容仅供研究参考，付费前请自行鉴别。如您付费，意味着您自己接受本站规则且自行承担风险，本站不退款、不进行额外附加服务；查看《如何避免下载的几个坑》。如果您已付费下载过本站文档，您可以点击 这里二次下载。
- 3、如文档侵犯商业秘密、侵犯著作权、侵犯人身权等，请点击“版权申诉”（推荐），也可以打举报电话：400-050-0827(电话支持时间：9:00-18:30)。
- 4、该文档为VIP文档，如果想要下载，成为VIP会员后，下载免费。
- 5、成为VIP后，下载本文档将扣除1次下载权益。下载后，不支持退款、换文档。如有疑问请联系我们。
- 6、成为VIP后，您将拥有八大权益，权益包括：VIP文档下载权益、阅读免打扰、文档格式转换、高级专利检索、专属身份标志、高级客服、多端互通、版权登记。
- 7、VIP文档为合作方或网友上传，每下载1次， 网站将根据用户上传文档的质量评分、类型等，对文档贡献者给予高额补贴、流量扶持。如果你也想贡献VIP文档。上传文档
查看更多
MMM10_γ-Alumina with hierarchically ordered mesopore-macropore from dual templates
Microporous and Mesoporous Materials 131 (2010) 289–293
Contents lists available at ScienceDirect
Microporous and Mesoporous Materials
journal homepage: www.elsevi /locate/micromeso
c-Alumina with hierarchically ordered mesopore/macropore from dual templates
Shao-Wei Bian 1, Yu-Liang Zhang, Hui-Ling Li, Yu Yu, Yan-Lin Song, Wei-Guo Song *
Beijing National Laboratory for Molecular Sciences (BNLMS), Institute of Chemistry, Chinese Academy of Sciences, Beijing 100190, PR China
a r t i c l e i n f o a b s t r a c t
Article history: In this paper, we report a procedure using soft/hard dual templates to produce c-alumina with hierarchi-
Received 1 October 2009 cally ordered mesopores and macropores (HOMA). Polystyrene spheres colloidal crystals and block co-
Received in revised form 5 January 2010 polymer are sequentially used as templates for ordered macropores and mesopores, respectively. Both
Accepted 8 January 2010
macropores and mesopores are ordered pores. The wall of cage-like 500 nm macropores is composed
Available online 13 January 2010
of ordered mesopores of 3.6 nm, and the walls of mesopores are composed of c-alumina. When loaded
with Pt nanoparticles for CO oxidation, Pt/HOMA catalyst shows excellent catalytic properties.
Keywords:
2010 Elsevier Inc. All rights reserved.