竹材径向压缩的蠕变行为.doc

竹材径向压缩的蠕变行为 张晓敏1，2 孙正军1 王喜明2 （1 国际竹藤网络中心，北京 100102；2 内蒙古农业大学材料与艺术设计院，呼和浩特 010019） 摘 要：用四元件的Burger粘弹性模型拟合了毛竹竹材在压力为6MPa时不同温度、含水率下径向压缩的蠕变行为，确定了模型中的4个元件参数。结果表明：在压应力小于屈服极限时，Burger模型可用来描述竹材径向压缩的短期蠕变行为； 4个元件模型参数受温度和含水率影响较大，实验结果表明： 四元件参数与含水率成反比关系，温度与瞬时弹性模量Ee成正比关系，与其他三元件参数成反比关系。 关键词： 竹片单元 径向压缩 勃格模型 元件参数 Creep Behavior of Bamboo Compressed on Radical Direction ZHANG XIAO MIN1,2, SUN ZHENG JUN1, WANG XI MING2 (1. International Center for Bamboo and Rattan, Beijing 100102,China; 2 Inner Mongolia Agricultural University ,Huhhot 010019, Inner Mongolia,China) Abstract: Burger model was used to imitate the radical compression creep behavior of bamboo (Phyllostachs edulis) under the different temperature，the moisture content．The four element parameters of Burger model were determined in this paper．The results showed that the creep behavior of bamboo was obtained by means of the Burger model in the yield strength scope．The experimental results show that: the four component parameters is inversely proportional to moisture content, temperature and the instantaneous elastic modulus Ee in direct proportional relationship While the other three components is inversely proportional to the temperature. Key words： Bamboo, Radical compression , Burger model , Element parameter 木材是可压缩的多孔固体材料，在径向和弦向具有类似高分子材料的粘弹行为，但本质是多孔材料的压缩。其粘弹行为受到温度、湿度、加载时间、加载速率和应变幅值等条件的影响。蠕变和应力松弛为粘弹性的两种典型加载模式。 我国对木材流变学的研究始于20世纪80年代中期，王培元研究了刨片的横纹压缩流变性能，结果表明：刨片易于受压变形，越薄，柔量越大，刨片厚度及刨片层叠方向都会影响到刨片流变性能。施建平等人用参数分离法研究了柞木的流变，结果表明：弹性变形与恒压应力成直线关系，瞬间塑性变形与其成几个阶段的直线关系，推迟弹性变形及依赖时间塑性变形都遵循以对数为主体的函数。卢宝贤等研究了粘弹性模型在木材蠕变中的应用。顾继友研究了人造板的变形及蠕变性能等，其成果对指导木基人造板生产及应用有重要意义。 相对木材而言，我国对于竹材粘弹性的研究却比较少。竹材是由维管束和薄壁细胞组织组成，也属于可压缩的多孔材料。但竹材的变异性大， 竹青部和竹黄部模量和强度有很大差距。在竹人造板及竹层积材生产中，很多质量缺陷都是与竹材在压缩过程中板坯内应力的产生和释放有关「1」 人造板生产中，构成单元的变形状态直接影响最终产品的质量，通常，木质人造板单元的粘弹性会导致成板的回弹，并引起内应力，产生较大的不可逆厚度膨胀率(顾继友,2003)。而人造板单元的粘性则直接影响成板的密度在厚度方向上的分布和内结合强度。所以，研究竹材在不同温度﹑不同含水率、不同方向压缩流变性能，对竹人造板加工及竹层积材的改进具有指导意义。基于此，本文以我国产量大，分布广的毛竹为原料，研究其在不同含水率和不同温度时径向压缩流变性能。 国家十一五科技支撑项目支持 通讯作者