最新Sr2CeO4Eu2+,Mn2+荧光粉发光性能的探究.docVIP

CQWU/JL/JWB/ZY084-02 学年论文 （课程论文、课程设计） 题 目：Sr2CeO4:Eu2+,Mn2+荧光粉发光性能的探究 2011 级 化 学 师 范 1 班 成 绩： 指导教师（职称）： 讲师 2013年5月26Sr2CeO4:Eu2+,Mn2+荧光粉发光性能的研究 摘要：用高温固相反应法制备了掺杂Eu2+的Sr2CeO4的荧光粉基质，并向基质中加入不用量的Mn2+后，用X射线粉末衍射、紫外可吸收光谱和荧光光谱等分析手段研究了荧光体的结构和光致发光性能。结果发现，Sr2Ceo4发光体的最大激发峰和最大发射峰分别在310nm和485nm左右，为有效的蓝光发射。用Eu2+做诱导剂会降低Sr2Ceo4发光体的发光强度，向Sr2Ceo4：0.02Eu2+X=0.01～0.06molMn2+后，荧光粉的发光强度会再次降低。从而得出结论，Mn2+不利于Sr2Ceo4：0.02Eu2+：Sr1.98-xCeo4：0.02Eu2+，Mn2+x[abstract]: Eu2+, Mn2+ doped Sr2CeO4 phosphor were prepared by high temperature solid state method, X-ray powder diffraction (XRD), ultraviolet absorption spectrum and fluorescence spectrum were employed to measure the properties of samples, the result shows that the maximum excitation and emission were 310 nm and 485 nm, which emitting blue light. Eu2 + doping can reduce the luminous intensity of Sr2CeO4. When we introduced Mn2+ into Sr2CeO4：0.02Eu2+, the luminous intensity of fluorescent powder reduced again. To the conclusion, Mn2 + is not conducive to Sr2CeO4：0.02Eu2+ phosphor. [key words]: Sr1.98-xCeo4：0.02Eu2+，Mn2+x；High temperature solid phase ; Luminescence properties 1 引言 稀土离子是一种特殊的掺杂中心, 研究其掺杂于发光基质材料中的发光行为具有重要的现实意义[ 1,2] 。Danielson 等人[3] 利用组合化学方法发现了高效的Sr2CeO4 蓝色发光材料, 引起了人们的关注[ 4，6]Sr2CeO4 中铈以Ce4+的形式存在，Ce4+无4f电子不能跃迁发光。但在室温下该发光体在254nm或365nm的紫外光激发下都能可发出明亮的蓝白色光。在其中掺杂合适的稀土离子和金属离子以寻找新型的发光材料引起了人们的重视。对稀土激活碱土铝酸盐长余辉材料发光机理的研究，从20世纪90年代初至今一直是一个热点课题，目前最有前途的、共掺辅助稀土激活离子的碱土铝酸盐长余辉材料MAl2O4：Eu2+，RE3+M为碱土金属，RE3+为起辅助集火作用的稀土离子）的长余辉发光材料就是一例【7-9】Sr2Ceo4：0.02Eu2+Mn2+在Sr2Ceo4：0.02Eu2+X=0.01~0.06mol的Mn2+的0.005molSr1.98-xCeo4：0.02Eu2+，Mn2+x荧光体将SrCO3与CeO2按2∶1 物质的量之比配置成0.005mol Sr2Ceo4的样品，作为第一个样品。将SrCO3、CeO2和Eu2O3按1.98:1:0.02物质的量配置成0.005mol的Sr2Ce4：0.02Eu2+样品，作为第二个样品。然后将SrCO3、CeO2、Eu2O3和MnCO3按照物质的量之比为1.98-X：1:0.02：X配置成0.005mol Sr1.98-xCeo4：0.02Eu2+，Mn2+x的样品，其中X=0.01～0.06将上面的8个样品分别在玛瑙研钵中充分研磨后装入坩埚,置于马弗炉,在800℃预烧3h然后研磨5～10min, 在1200℃的H2气氛中灼烧还原4h，研磨成细小的粉末，为最终产品。 采用日本理学D/ MAX23A 2 型X 射线粉末衍射仪(