23MnNiMoCr54链条钢焊接断裂原因分析 赵亚娟 陶涛 田力 (南京钢铁股份有限公司技术质量部，南京 210035) 摘要： 23MnNiMoCr54链条钢在使用过程中从焊缝接头处发生了断裂，本文对产生断裂的现象进行了详细分析，运用光谱仪、氧氮分析仪、扫描电镜和电子探针等仪器对试样进行了观察，研究。结果表明，试样的化学成分、低倍分析、硬度分析均满足国标要求，断裂发生在焊缝处，是由于外来Cu的进入引起晶界弱化，晶界强度急剧下降，导致焊接接头处发生断裂，为此，应对焊接工艺过程进行严格规范控制，提高焊缝处质量。 关键词：23MnNiMoCr54链条钢，焊接，Cu热脆 中图分类号：TG142.1+5 文献标识码：A 文章编号：1001-0777(2013)??-????-?? Fracture Analysis of Welded 23MnNiMoCr54? Steel Chain ZHAO Ya-juan TAO Tao TIAN Li (Technology Quality Department of Nanjing iron and Steel Co. Ltd, Nanjing 210035,Jiangsu,China) Abstract: 23MnNiMoCr54 ?chain steel fractured in the weld joints in use processing, the?fracture?phenomenon was detailed analyzed in the paper, using spectrometer,?oxygen nitrogen analyzer,?scanning electron microscope and?electron probe?instrument to study, results show that, the chemical composition,?sample?analysis of the low magnifications, hardness?can meet the national standard requirements, ?the fracture occurred in the?weld,?the?foreign Cu?into the?lead to?grain boundaries, and grain boundary?strength decrease sharply,?leading to fracture, so occurrence of?welded joints?for?welding process,?should?strictly regulate?controlled to improve?the quality of?weld. Key words: chain steel of 23MnNiMoCr54，welding，hot brittleness of Cu 前言 23MnNiMoCr54链条钢具有高强度、高韧性，良好的耐疲劳性和冷弯性能，在我国矿业、重型运输机械等行业广泛应用。其中焊接作为圆环链生产的关键工序之一，由于闪光对焊方法具有省时、省料、省能源等诸多优点而常常被采用[1-3]。但如果焊接工艺控制不当容易日后使用过程中发生断裂等问题。最近，某厂生产的23MnNiMoCr54链条钢在用户的使用过程中，个别试样从焊缝接头处发生断裂，为此，本文从多方面进行了系统的分析，以找出断裂的原因。 作者简介：赵亚娟（1980—），女，硕士研究生，高级工程师；E-mail：zhaoyajuan@； 联系电话 无基金项目 1 试验与分析 焊接试样的链条钢生产工艺为：坯料验收→步进炉钢坯加热→高压水除鳞→粗轧→1#飞剪→中轧→2#飞剪→精轧→3#飞剪→冷床冷却→定尺剪切→缓冷→退火→矫直→剥皮或酸洗修磨→探伤→成品检验→包装→标识→称重→入库，开轧温度目标值为1100±40℃，终轧温度950~1000℃，工艺控制符合要求。 1.1 化学成分分析 对试样的断口附近取样，运用ARL 4460OES Metals Analyzer光谱仪进行化学成分分析，运用HORIBA OXYGEN NITROGEN ANALYZER EMGA-620W氧氮仪进行O、N气体分析，结果如下表1，化学成分符合标准要求范围，五大有害元素在控制范围之内，O、N气体含量较低。 表1 23MnNiMoCr54链条钢的化学成分，wt% Table.1 The chemical composition of 23MnNiMoCr54 chain steel,wt% C Mn P S Si Ni