alcti体系自蔓延焊接钛合金实验分析word格式论文.docxVIP

Al - C - Ti system self-propagating welding titanium alloy experimental researchAbstract:SHS welding is a new application field using self-propagating high-temperature synthesis technology, SHS using quantity of heat reactions release of itself and product to achieve the same or dissimilar material welding. The influence of self- propagating welding contain many factors, including the raw material composition and reaction process parameters of the experiment etc.This experiment will choose Al - C - Ti powder system as self-propagating reaction system to carry out welding experiments, from the experiments we can get:（1）When thepercent of aluminum from twenty increased to forty in the system, the product only contains Al, C and TiC, when the percent of aluminum increased to sixty percent, the percent of product of Al obviously increased, also appeared Al3Ti phase. And with the increase of the percent of Al, grain size of TiC obviously decreased, when the percent of aluminum increased fifty percent , the particle size of TiC decreases to one microns. And the welding effect changes with the increased of the percent of aluminum, welding is best when the systemcontent forty percent of aluminum. （2）When the C/Ti atoms ratio from zero point sixincreased to zero point eight ,the SHS product include Al、Ti C and Al3Ti phase, when the C/Ti atoms ratio ,the product of SHS include Al and Ti C phase. When the C/Ti atoms ratio iszero point seven, there are a lot of branch shape of Al3Ti, only a little of TiC, with the increases of C/Ti atomic ratio, the branch shape Al3Ti gradually decrease, the amount of TiC Increase gradually, and the has morpholo- gy of Al3Ti changed, from branch shape into a mass- ive shift gradually. With theincreases of C/Ti atomic ratio, the porosity of SHS product in- creased significantly, the densify decline, welding is best When C/Ti atomic ratiois 1.0. （3）With the increase of relative density, the particle size of TiC is decreased in theSHS synthetic pr