ZHPb59-1铅黄铜精炼等级的快速判定方法及其原理(铸造技术,08年第2期).doc

ZHPb59-1铅黄铜精炼等级的快速判定方法及其原理 解建会 江门吉事多卫浴有限公司，广东江门，529075 摘要：ZHPb59-1铅黄铜因良好的铸造性能而在卫浴产品中有广泛的应用，而其精炼状况又对其铸造性能有重要的影响。本文通过对不同杂质元素含量、精炼剂含量、冷却速度及浇注方式下，铅黄铜宏观与显微组织的变化进行分析，介绍一种对ZHPb59-1铸造铅黄铜的精炼状况进行炉前快速判定的方法及其原理，进而指导铜水熔炼作业及其快速判定，改善铸造性能。 关键词：铅黄铜；晶粒细化；宏观组织；微观组织；结晶带； Speedy judgment method and principle for grain refine class of ZHPb59-1 Xie jian hui Giessdorf plumbing inc, JiangMen,GuangDong, 529075 Abstract: studing the grain refine status of ZHPb59-1 under the influence of the contents of impurity,the content of refine agent,the cooling speed and the method of pouring.and find the relationship between the marcostructure and the microstructure.this help us to use marcostructure of the sample speedy judgment the grains refine status without microstructure check.This method and principle raise the melting efficiency and ensure the quality of the liquid metal. Key words: lead brass; grain refine; marcostructure; microstructure; crystallization belt; CuAlB精炼剂在ZHPb59-1铅黄铜熔炼过程中经常使用，一般以B的加入量为8~12PPM为宜。另外，ZHPb59-1铅黄铜对Sn、Fe、Ni等杂质元素量也有严格的限定，因为杂质元素如同B一样，不同含量对精炼效果有不同影响。生产中，不同的冷却速度及浇注方式，对铜水精炼效果也有一定的影响。本文引用一种利用黄铜锭的宏观组织快速判定铜水精炼状况的方法及其原理，并对相关因素对ZHPb59-1铅黄铜精炼效果的影响进行了研究。 一、ZHPb59-1铅黄铜精炼等级快速判定方法 1、试验用检测工具、仪器、化学药品 1．1、用铍铜制作试样铜锭模，铜锭横截面尺寸为：60/80*30，长度200mm，铜锭模壁厚约25mm； 1．2、用精度1克的天平、500ml的量筒分别称量过硫酸铵及蒸馏水； 1．3、用分析纯的过硫酸铵，配制金相腐蚀液，用来观察铜锭试样的宏观与显微组织； 1．4、按实际生产流程抛制金相试样。在金相显微镜下观察。宏观组织在10X以下，显微组织为200X。 2、金相试样制备 2．1、取样：将铜锭模预热至130℃左右，铜水调至要求成份并保持温度在1000℃～1030℃； 2．2、用浇铸勺，手工舀取适量铜水缓慢浇注到铜锭模，冷却至600℃以下出模，空冷至室温； 2．3、将所得铜锭样品，从横截面处切断，按以下流程抛光﹕80＃砂 ＃砂 400＃砂 麻轮 布轮150g＋蒸馏水1000ml.，浸蚀时间约2分钟。 3、精炼等级判定标准 3．1、浸蚀试样的宏观组织，用肉眼即可快速判定。一般有如下几种状况（图1-1所示）： 图1-1A 图1-1B 图1-1C 图1-1D 图1-1E 图1-1、试样各类宏观组织图 3．2、宏观组织判定的标准，如表1-1所示： 表﹕标准 等级 说 明 备 注 0 外侧为较大的八面体晶粒构成的连续均匀的边缘结晶带﹐内部为肉眼难以判断的均匀致密的结晶区域﹒属精练最佳的黄铜锭﹒ 1 外侧为较大的八面体晶粒构成的间断的均匀的边缘结晶带﹐内部为肉眼难以辨别的均匀致密的结晶区域﹒属精练欠佳的黄铜锭﹐重熔时﹐晶粒有可能变得粗大﹒ 2 没有边缘结晶带﹐整个断面为肉眼可以但不易辨别大小的晶粒﹒属稍作精练的黄铜锭﹐重熔时﹐晶粒会变得粗大﹒ 3 没有边缘结晶带﹐整个断面为肉眼较易辨别大小的晶