低成本高性能膜砂用酚醛树脂的研讨.pdfVIP

摘 要 摘 要 本文通过添加双醛的方法来解决热塑性酚醛树脂合成过程中游离酚含量偏高的问 题。利用正交试验方法，解决添加双醛的种类和比例、反应时间以及脱水温度等问题。 使游离酚含量从 10%下降到 2% 以内，增加反映转化率，降低合成成本，通过改性处理 使树脂具有较高的粘接强度，提高树脂砂的抗拉强度，研究抗拉强度随酚醛树脂加入量、 烧结时间和烧结温度之间的关系。 关键词 双醛 酚醛树脂 游离酚 I Abstract Abstract Synthesized from adding dialdehyde to solve the problem which more free phenol in phenolic resin. By means of orthogonal empirical approach to determine which dialdehyde we will use and the addition of that dialdehyde. We will make sure the reaction time and the dehydration temperature. We tried to descent free phenol in phenolic resin from 10% to 1-2% , to increase percent conversion, to lower the costs of production. Through modification we want to raise bonding strength of the phenolic resin, to obtain high tensile strength of tectorial membrane on the sand. Researching the tensile strength between the quantity of phenolic resin added、the sintering time and the sintering temperature. Keywords dialdehyde phenolic resin free phenol II 第 1 章 绪论 第 1 章 绪论 1.1 酚醛树脂产生的背景 酚类化合物与醛类化合物缩聚而得的树脂统称为酚醛树脂。其中以苯酚与甲醛缩聚 而得的酚醛树脂最为重要。 酚醛树脂是最早人工合成的聚合物。1872 年德国化学家拜耳（A ．Bayer ）首先发现 酚与醛在酸的存在下形成树脂状产物。1910 年巴克兰提出了关于酚醛树脂“加压、加热” 固化的专利，成功地确立了通过“缩合反应”即在施加高压的情况下，使预聚体发生固 化的技术。他还明确指出，酚醛树脂是否具有热塑性取决于苯酚和甲醛的用量比，以及 所用催化剂类型，并介绍采用木粉或其他填料可以克服树脂性脆的缺点，实现了酚醛树 脂的实用化和工业化生产。1911 年艾尔斯沃思（Ayleswbrth ）发现应用六次甲基四胺可 使酚醛树脂固化；1913 年德国科学家阿尔贝特（K ．Albert ）发现了油溶性酚醛树脂的 制造方法，为合成树脂在涂料工业的应用带来了极大的推动力，从而确立了重要的地位。 酚醛树脂及塑料作为一种原料易得、价格低、性能优异的品种，至今已有将近百年 的历史，面对航天、航空、电子工业、汽车工业等高新技术领域的需要，科学工作者为 充分发挥酚醛树脂的固有潜力，在其高性能方面又做了大