AbstractAs for low strength of joint of 7A52 aluminum alloy by double wire MIG, ap- plying ultrasonic impact treatment on superficial weld joint under the condition of 2A preset current, the impact velocity of 0 ~1.25min/cm2.Observing and analyzing the microstructure, hardness and wear resistance of 7A52 aluminum alloy welded joint before and after ultrasonic impact treatment by means of optical microscope, XRD, scanning electron microscopy, transmission electron microscope, microhardness tester and so on. It was found that nanocrystalline organization could be got in 7A52 aluminum alloy welde