SSPCPA1油漆应用技术规范第1部分,钢材车间,现场及修补喷漆.ppt

Curing and Handling of Coating 涂料的固化与处理 干燥时间：表干, 硬干 硬干≠ 完全固化 Curing and Handling of Coating 涂料的固化与处理 涂料固化过程的保护，防止雨水、冷凝、污染、雪和冻结等等。缺乏适当的保护措施可能导致涂料的早期失效。 Curing and Handling of Coating 涂料的固化与处理 QA SSPC PA1 SSPC PA1: PAINT APPLICATION SPECIFICATION NO. 1 Shop, Field and Maintenance Painting of Steel SSPC PA1: 油漆应用技术规范 第1部分，钢材车间，现场及修补喷漆 This specification covers procedures for the painting of steel surfaces. This specification does provide detail coverage of the procedures and methods for application after the selection of the coating materials has been made. 本规范覆盖钢材表面的喷漆所用的程序。本规范为选择涂料之后的涂装程序和方法提供了详细的说明。 SSPC PA1 Pre-Application Procedures 预备涂装程序 Factors Affecting Application of Coating涂料施工的影响因素 Application Methods 涂装方法 Shop Coating车间涂装 Field Coating现场涂装 Repair of Damaged Intact Coating修补损坏的涂层 Application Procedures for Generic Groups of Coating 通用组别涂料的涂装程序 Curing and Handling of Coating 涂料的固化与处理 Pre-Application Procedures 预备涂装程序 Pre-Application Procedures 预备涂装程序 检查油漆桶是否完好无损。 检查油漆桶上是否有清楚的标签，表明涂料名称，生产日期，批号等信息。 开罐检查油漆状态是否均匀，是否溶剂搅拌，是否有无凝胶化等。 为开封的油漆，通常需要保持在4－38度的通风的室内环境。 Pre-Application Procedures 预备涂装程序 表面处理的内容 钢结构缺陷的处理 表面处理的对象 锈蚀和氧化皮 盐份 油脂 灰尘／砂粒 旧涂层 目的获得适当的待涂装表面 表面处理的方法 溶剂清洗SSPC SP1 喷砂处理SSPC SP6 手工或动力工具处理SSPC SP2 。。。 钢结构缺陷处理 钢板表面的起鳞，打磨光滑 焊缝咬边，补焊并打磨 手工焊缝的毛刺，打磨光顺 钢板切割面要打磨光顺 Pre-Application Procedures 预备涂装程序 溶剂处理 溶剂清洗油污的工作应该在喷砂施工前完成 Pre-Application Procedures 预备涂装程序 用于抛丸和车间内喷砂用的钢砂／钢丸 钢砂： 具有切割作用 产生很好的表面粗糙度 钢丸： 切割作用较小 延长设备使用寿命 可以硬化金属表面，减少应力腐蚀的发生 Pre-Application Procedures 预备涂装程序 开放式喷砂使用的磨料 喷射用磨料要干燥，清洁无杂物，不能对涂料的性能有影响。 所选用的磨料应当符合ISO 11126 1-8的规定，并根据11127 1－7进行测试。 磨料的推荐直径为0.8-1.2，能够产生规定涂料系统要求的粗糙度。 Pre-Application Procedures 预备涂装程序 喷砂清理的表面 表面漏喷，返黄， 有氧化皮存在都 是不可接受的 Pre-Application Procedures 预备涂装程序 涂料的混合 对于双组分高性能涂料 先搅拌A组份 再加入固化剂 搅拌均匀 稀释剂的加入量 在有适当设备下，可不加稀释剂 加入适当的稀释剂，可改善施工性能 过渡稀释，可导致流挂，低膜后，低遮盖等的问题。 Pre-Application Procedures 预备涂装程序 Factors Affecting Application of Coating涂料施工的影响因素 环境因素： 温度：过高或过低的温度都可能限制涂料的施工 水分：有雨、风、雪、雾或