转炉内衬新型湿法遥控喷补技术 邓乐锐 董战春 章荣会 （北京联合荣大工程材料有限责任公司北京 怀柔 101400） 摘要：通过对湿法喷射设备的改进和对镁硅质自流料性能的调整，实现了镁硅质自流料的喷射施工。该项 技术应用到转炉内衬修补上，与传统湿法喷补和目前国内普遍采用的半干法喷补技术相比具有需水量极低， 喷补层结构致密，使用寿命高等优点；与干法喷补料（树脂、沥青结合）相比，烧结过程不会产生有毒气 体，绿色环保。预计会有良好的发展前景。 关键词：转炉；遥控；湿法喷补 New Remote Shotcrete Gunning-repair Technology for Converter Lining Denglerui Dongzhanchun Zhangronghui (Beijing Allied Rongda Engineering Material Co.,Ltd. Beijing 101400,China) Abstract: Through the improvement of wet-gunning equipment and the adjustment of magnesium and silicon self-flowing material’s performance, the magnesium and silicon self-flowing material shotcrete construction is realized. The technology is applied to repair converter lining, and compared with traditional wet gunning-repair and semi-dry gunning generally used in China at present the technology has such advantages as low water demand, compact gunning-repair structure and long service life; compared with dry spraying-repair materials (bonded by resin and asphalt), none toxic gases will be produced during its sintering process, as a result it is green environmental protection. It is expected to have good development prospect. Key words:converter ；telecontrol ；wet gunning-repair 1. 前言 为了延长转炉寿命，对转炉进行喷补已经有近50 年的历史，喷补技术在实践中不断得 到改进。喷补方法先后出现过湿法，干法，半干法和火焰喷补法。各种方法都有其特点，都 [1] 在不同程度上延长了转炉寿命 。 传统的湿法喷补技术由于喷补料浆水分太高，既对炽热砖衬有损害，又因水分快速挥发 [1] 导致喷补层气孔率高、强度低、抗渣性差等 。基本已被半干法取代。目前，国内转炉喷补 大多为半干法喷补，该法因设备简单，操作方便而得到了较大范围的推广。但由于该喷补料 多以磷酸盐或硅酸盐作为结合剂，导致材料高温性能劣化，耐侵蚀性能差，需要频繁进行炉 [2] 况维护，影响耐火材料消耗和转炉作业率 。同时，半干法也存在和传统湿法喷补同样的需 水过多的问题。干式喷补料以沥青或树脂等有机物做结合剂，并加入抗氧化剂，无需加水， 直接喷补到热的炉衬上即可达到良好的粘接效果，不但很好的解决了传统湿法和半干法水分 过多和添加无机盐带来的不良影响，也较好的满足了转炉炉况维护要求，保证转炉生产高