锈蚀钢筋与混凝土粘结性能研究.docVIP

锈蚀钢筋与混凝土粘结性能研究 　　【摘 要】钢筋锈蚀是引起混凝土结构耐久性劣化的主要原因之一。锈蚀使钢筋与混凝土的粘结性能发生退化,严重地降低了钢筋在混凝土结构中的作用,甚至导致混凝土结构的坍塌破坏。研究锈蚀钢筋粘结性能的退化规律对于已建混凝土结构的耐久性评估具有重要的意义。该文在既有研究的基础上,通过锈蚀钢筋粘结性能试验,对锈蚀钢筋的力学性能和粘结性能的退化规律进行研究。 　　 　　【关键词】钢筋;锈蚀;粘结性能;耐久性 　　 　　Corrosion of steel and concrete properties of the bonded 　　Yang Song-rong,Sun You-tai 　　(Zhejiang BoYu Building Co.,Ltd. Zhoushan Zhejiang 316000) 　　【Abstract】Corrosion of reinforced concrete structures is caused by deterioration of the durability of one of the main reasons. Corrosion of the reinforcement and the adhesive properties of concrete degradation, seriously reducing the reinforced concrete structure in the role, and even lead to the collapse of the destruction of concrete structures. Study on Bond Behavior of Corroded Reinforced for the degradation of the law has been built to assess the durability of concrete structures is of great significance. In this paper, the existing research on the basis of the bond behavior of corroded reinforced through experiments on the mechanical properties of steel corrosion and degradation of the performance bond to study law. 　　【Key words】reinforcement;corrosion; bondbehavior;durability 　　 　　1. 概述 　　 　　混凝土中钢筋锈蚀是十分普遍的现象,尤其是在沿海地区、工业污染地区钢筋锈蚀问题更为突出。如今钢筋锈蚀已被公认为混凝土结构耐久性劣化最主要的原因,不少国家为此遭受了巨大的经济损失。 　　混凝土中锈蚀钢筋的粘结性能随锈蚀率的变化而变化,并与多种其它因素有关。钢筋与混凝土之间的传力是通过它们之间的粘结作用完成的,粘结性能的好坏直接影响到钢筋的锚固性能和混凝土裂缝的开展,良好的粘结性能使钢筋在一定的传递长度(锚固长度)内达到屈服强度且留有余地,对于确保结构的安全有着十分重要的意义。 　　混凝土中钢筋锈蚀对结构性能的影响除了表现为钢筋截面削弱外,更重要的是锈蚀产物对钢筋与混凝土粘结性能的影响。钢筋锈蚀破坏了钢筋与??凝土之间原有的状态,使它们之间的粘结性能发生改变,这种粘结性能的变化是十分复杂的,它不仅与锈蚀程度密切相关,而且与钢筋种类、混凝土保护层厚度等因素也有着密切的关系。锈蚀钢筋粘结性能的变化对构件的受力性能产生很大的影响,严重时甚至使结构丧失承载力而破坏。因此深入研究锈蚀钢筋的粘结性能,找出其退化规律,对于钢筋混凝土耐久性评估和结构的维修加固都有着重要的意义。 　　 　　2. 钢筋与混凝土的粘结机理 　　 　　一般认为钢筋与混凝土之间的粘结力由三部分组成: 　　(1)混凝土中的水泥凝胶体与钢筋表面的化学胶着力。它取决于水泥的性质和钢筋表面的粗糙程度。 　　(2)钢筋与混凝土接触面上的摩擦力。它取决于混凝土发生收缩和荷载作用等引起的径向压力,以及二者间的摩擦系数等。 　　(3)钢筋表面粗糙不平产生的机械咬合力,即混凝土对钢筋表面斜向压力的纵向分力。机械咬合力的极限值受混凝土的抗剪强度控制。 　　实际上钢筋与混凝土的粘结机理相当复杂,对于不同类型钢筋,粘结机理不尽相同,它们表现出来的粘结性能也不同;对于后张法 PC 结构,由于锚具、管道及管道灌浆的存在,预应力钢筋的粘结机理和粘