《水性UV油墨的配置与性能研究》毕业学术论文.doc

PAGE 摘 要 水性UV油墨主要是由预聚物（水基光固化树脂）、光引发剂、颜料、胺类物质、水、助溶剂和其它添加剂等配制而成。其结合了UV油墨和水性油墨的优点，拥有比单独UV油墨或水性油墨更好的印刷适性。其干燥固化结合了UV光固化和水性油墨渗透蒸发二种干燥形式，具体说主要有两种干燥方式：水性体系的预挥发干燥和紫外光固化。这是一种新型的环保型UV油墨，主要应用于PET塑料表面的印刷。 水性UV光油以水和乙醇作为稀释剂，其干燥速度、附着力等都受到水性UV光固化树脂在光油中所占比例的影响，实验需通过不断改变水性UV光固化树脂的比例来测试水性UV光油的固化性能，综合各个参数，寻求最佳配比。 通过在最佳比例的水性UV光固化树脂的条件下，配制水性UV光油，改变添加剂的种类、含量，颜料的种类及含量后，研磨油墨后以丝网印刷的方式，通过300目/cm，绷网张力在20N/cm以上的丝网印刷在PET塑料表面，测试其干燥速度和油墨附着力，并通过不断改变实验条件来改善其干燥速度和附着力。 关键词：水性UV油墨 最佳配比 干燥速度 附着力 ABSTRACT Water character UV printing ink is mainly made up with prepolymer（water-base photo-curing resin）、Light initiator 、Pigment 、Amines material, water, flux and other chemical additives and so on . It unified the UV printing ink and t Water color ink merit, has compared to alone the UV printing ink or Water character printing ink better printability. Its dry solidification unified the UV photo-curing and Water color ink penetration evaporates dry forms, said specifically mainly has two dry ways: Water character systems pre-volatility dry and ultraviolet photo-curing. This is one kind of new environmental protection UV printing ink, mainly applies in PET plastic surface printing. The water character UV gloss takes the diluent by the water and the ethyl alcohol, its drying velocity, the adhesion and so on receive the water character UV photo-curing resin to account for the proportion in the gloss the influence, The experiment must through change the water character UV photo-curing resin the proportion to test the water character UV gloss unceasingly the solidification performance, synthesizes each parameter, seeks the best allocated proportion. Through under best proportion water character UV photo-curing resin condition, disposition water character UV gloss, change chemical additive type, content, after pigments type and content, after abrasive ink, by silk-screen printing way, Through 300 item /cm, stretches the net tensity in the 20N/cm above silk-screen printing in the PET plastic surface, tests its dr