检 Test and Measurement Technique 测 技 术 铸铁件超声波检测方法的应用和发展 朱 丹，曾效舒 （南昌大学 机电工程学院，南昌 330031） 摘要： 介绍了国内外超声波检测技术在铸铁件上的应用和发展，简述了利用超声波技术检测灰铸铁和球墨铸铁共晶度、 抗拉强度、球化率和蠕化率的方法，以及铸铁件的缩孔、缩松、气孔、偏析、夹砂、裂纹等常见缺陷的区分方法。 关键字：铸铁件；缺陷；超声波检测 中图分类号： ， 文献标识码： 文章编号： （ ） TG25 TG115 B 1003－8345 2009 05－0076－04 Application of Ultrasonic Test to Iron Castings and Its Development ZHU Dan, ZENG Xiao-shu （Mechanical and Electrical Engineering College, Nanchang University, Nanchang 330031, China） Abstract: The application of ultrasonic test technique to inspect iron castings and its development in China and abroad was introduced. A brief description was made to the methods of using ultrasonic technique to inspect the carbon saturation degree and tensile strength of gray, nodular cast irons, to inspect the nodularity and vermicularity, as well as to differentiate the common defects of iron castings such as shrinkage cavity and porosity, blowhole, segregation, scab, cracking and so on. Key words: iron castings; defect; ultrasonic test 1 铸铁件超声波检测技术的发展 的结论。但结晶粒度会使声能被迅速衰减；反射 波与连续波反相，信号被削弱，易产生假信号，以 超声波检测的原理是利用超声波在工件中 致根本无法实现铸铁件的检测。直到1942 年英 的传播、反射、折射、波形变换等物理现象来分析 国D O Sproule 和美国F A Firstone 发明的脉冲 [1] 材料内部的结构状态 。尽管早在 1929 年和 回波系统解决了连续波的检测问题，但由于声束 1931 年，俄国和德国科学家已经提出使用超 在固体中存在波