水泥混凝土桥面沥青铺装结合面抗剪性能的研究 　　【摘 要】本文在室内对由高粘4#沥青制成的标准试件进行直剪试验,获得了水泥混凝土桥面沥青铺装结合面抗剪强度随混凝土界面粗糙状况、试验温度的变化规律,并确定了高粘4#沥青的最佳材料用量,可供广大工程技术人员参考。 　　【关键词】沥青混凝土;结合面;标准试件;剪切强度;回归方程 　　Combination of concrete bridge decks with asphalt pavement performance of Shear 　　Li Wei-dong 　　(Anhui Vocational and Technical Education, Department of Civil Engineering Hefei Anhui 230051) 　　【Abstract】This paper inside of the asphalt produced by the high viscosity 4 # standard direct shear test specimens obtained by combination of concrete bridge decks with asphalt pavement with concrete interface shear strength of rough conditions, test temperature variation, and 4 # asphalt determined the best high viscosity materials consumption, for the engineers and technical personnel for reference. 　　【Key words】Asphalt concrete; Joint surface; Standard specimen; Shear strength; Regression equation 　　1. 概述 　　沥青混凝土桥面铺装与正常路面和水泥混凝土桥面铺装相比,损坏形式又有所不同,主要有:(1)铺装层内部产生较大的剪应力,引起不确定破坏面的剪切变形,或者由于铺装层与桥面板层间结合面粘结力差,抗水平剪切能力较弱,在水平方向上产生相对位移发生剪切破坏,产生推移、拥包等病害;(2)因温度变化并伴随桥面板或梁结构的大挠度而产生的裂隙,在车辆荷载及渗入的水的作用下产生面层松散和坑槽等破坏。 　　本文在室内进行模拟试验,以确定沥青混合料在混凝土桥面铺装结构中的层间抗剪强度,以及研究其所处的结合面环境条件对沥青材料抗剪切的影响规律,以供正确指导水泥混凝土桥面沥青铺装层的设计与施工。 　　2. 试验方案 　　本室内模拟试验主要为直接剪切试验,试验过程中以4个试件为一组,取一组的平均值作为试验结果。 　　为了准确研究高粘沥青的界面抗剪切强度,全面分析各试验影响因素对剪切强度的影响规律,由此制定直剪试验方案如下: 　　(1)确定高粘沥青的最佳用量。对高粘-4#沥青在一定的范围内变动其用量,其它试验参数不变,进行结合面直接剪切试验,从而确定高粘-4#沥青的最佳用量; 　　(2)对3种不同水泥混凝土结合面粗糙状态(光滑、拉毛、嵌石),制成的复合试件,进行直剪试验,研究水泥混凝土结合面粗糙度对抗剪强度的影响; 　　(3)在不同的温度下,进行直剪试验,考察温度对结合面抗剪切强度的影响。 　　3. 材料选择 　　将试验试件做成“水泥混凝土+粘结层+沥青混凝土”的复合试件。试件中所用水泥混凝土的配合比为水泥:砂:石:水:外加剂=51:795:970:162:12。 　　粘结层选用高粘4#沥青,其主要技术指标见表1。 　　采用的SMA13为复合试件的沥青混凝土。其配合比和马歇尔各项技术指标见表2、表3。 　　3. 试件制备与试验装置 　　本试验自行研制的剪切仪是马歇尔稳定仪,要求试件为圆柱形芯样,,并且要求试件尺寸近似于标准马歇尔试模大小,即φ101.6mm×87mm的圆柱体试件,如图1所示。试验装置如图2所示。 　　表2 SMA-13沥青混凝土配合比 　　混凝土类型集料9.5～13.24.75～9.54.75～9.50～2.36矿粉水泥油石比 　　SMA-1340.5315129.526.3% 　　表3 沥青混凝土各项技术指标 　　混凝土类型密度空隙率矿料间隙率饱和度稳定度(KN)流值(0.1mm) 　　SMA-132.3733.617.278.97.1948.7 　　图1 标准试件图2 实验装置 　　4. 实验结果 　　试验时需观察记录的剪切特性包括材料、界面、环境因素影响下的破坏面情