筋桁架模板的应用技术 　　【摘 要】钢筋桁架模板既具有预制板的施工快速的优势,又具有现浇板整体刚度大,抗震性能好的优点，钢筋桁架模板组合结构楼板体系,作为钢结构建筑系统的重要组成部分,国外已有较长时间的应用经验,但在国内则应用时间短、经验少，本文对钢结构中钢筋桁架模板组合结构楼板体系的应用进行技术和经济等研究。 　　【关键词】钢结构；钢筋桁架模板；砼组合楼板 　　application technology of Steel bar truss slab deck 　　Tang Fei,Yuan Hui 　　(Schenck Process (Tianjin) Industrial Technology Co., Ltd Tianjin 300385) 　　【Abstract】Steel bar truss slab deck not only have high construction speed, but also have good earthquake-resistance and high stiffness as newly poured concrete slab.,it will be an important kind of construction structure.The structure of composite deck slab, as an important component of steel structure building, has been applied for long time , and rich experience is accumulated at abroad., But at home , its application time is short, and experience is lack. It has practical significance the technology and economy research on application of Steel bar truss slab deck in steel structure building. 　　【Key words】Steel structure;Steel bar truss slab deck;Sheeting-concrete composite slabs 　　1.钢筋桁架模板简介 　　1.1 产品概况：钢筋桁架模板是将楼板中钢筋在工厂加工成钢筋桁架，并将钢筋桁架与底模连接成一体的组合模板。见图1。钢筋形成桁架，承受施工期间荷载，底模托住湿混凝土，因此这种技术可免去支模的工作及费用。 　　1.2 产品形状：如图1 　　图1 钢筋桁架立面钢筋桁架剖面 　　1.3 构件规格：钢筋桁架模板是由钢筋桁架、支座钢筋、底模等构件构成。钢筋上下弦采用成盘供应得热轧钢筋HPB235、HRB400或冷轧带肋钢筋550级；腹杆采用成盘供应得HPB235、冷轧光圆钢筋550级或650级；桁架支座钢筋用热轧钢筋HPB235或HRB335。底模柴用镀锌卷板，基板厚度为0.5mm，镀锌层两面总计不小于120g/m??2。 　　1.4 节点设计：（如图2部分节点） 　　图2 　　2. 钢筋桁架混凝土楼板受力特点 　　2.1 普通现浇钢筋混凝土楼板，施工阶段因下部支模故基本没有挠度，待混凝土达到一定强度后拆模，在自重作用下，楼板下挠，板底混凝土产生拉力、甚至出现裂缝。而钢筋桁架模板根据是否设临时支撑分为两种情况： 　　2.1.1 设临时支撑时，与普通现浇混凝土楼板基本相同。（前期做好设计，基本不会出现） 　　2.1.2 不设临时支撑时，在混凝土结硬前，楼板强度和刚度即钢筋桁架的强度的刚度，钢筋桁架模板自重、混凝土重量及施工荷载全由钢筋桁架承受。混凝土结硬是在钢筋桁架模板变形下进行的，所以楼板自重不会使板底混凝土产生拉力，在除去楼板自重以外的永久荷载及楼面活荷载作用下，板底混凝土才产生拉力。这样，楼板开裂延迟，楼板的刚度比普通现浇混凝土楼板大。 　　2.2 在使用阶段，钢筋桁架上下弦钢筋与混凝土一起共同工作，此楼板与钢筋混凝土叠合式楼板具有相同的受力性能，虽然受拉钢筋应力超前。 　　3.施工过程中操作要点 　　3.1 深化设计： 　　3.1.1 根据设计图纸中梁的排部，确定最大无支撑间距；结合现浇混凝土楼板荷载情况，通过计算确定上、下弦钢筋及底模规格。 　　3.1.2 根据主结构形式确定排板方向。 　　3.1.3 根据桁架模板的规格，确定与主结构的搭接长度及搭接形式。 　　3.1.4 确定横纵向悬挑及收边形式。 　　3.1.5 确定单块模板长度。