磁场对复合乳化剂苯胺微乳液聚合体系相行为及其产物性能的影响研究化学工程与技术专业论文.docx

重庆大学硕士学位论文英文摘要 重庆大学硕士学位论文 英文摘要 PAGE PAGE IV was increased by the MF, and with the decrease of the Sm, the effect of MF on the microemulsion system was weakened. The characterization result of cyclic voltammogram(CV) showed that the CV property of the polyaniline prepared by microemulsion polymerization in the presence of composite emulsifier was better than that prepared in the presence of single emulsifier (SDBS or TX-100). Conductivityand XRD analysis result indicated that the PANI synthesized in the presence of MF there is significant on the crystalline degree and the conductivity properties. UV results indicated that the interaction force between molecules reduced, the delocalization of molecular chain increased, and the main characteristic absorption peaks of the PANI prepared in the presence of MF had the trend of moving to low-frequency due to the orientation of MF. Keywords: Polyaniline, Phase behaviors, Magnetic field, Electrochemistry 重庆大学硕士学位论文目录 重庆大学硕士学位论文 目 录 目 录 中文摘要I 英文摘要 II 1 绪 言 1 1.1 微乳液 1 1.1.1 微乳液的定义和分类 1 1.1.2 微乳液体系的形成机理 2 1.1.3 微乳液体系的制备方法 3 1.1.4 微乳液在聚苯胺合成中的应用 3 1.1.5 微乳液相行为研究 4 1.2 表面活性剂 6 1.2.1 离子型表面活性剂 6 1.2.2 非离子型表面活性剂 7 1.2.3 混合表面活性剂 7 1.3 导电聚苯胺 8 1.3.1 聚苯胺的合成 8 1.3.2 聚苯胺的聚合机理 9 1.3.3 聚苯胺的应用 10 1.4 磁场在聚苯胺合成中的应用 12 1.5 本课题的研究内容、目的及意义 13 1.5.1 本课题的目的、意义及创新点 13 1.5.2 本课题的研究内容 14 2 试验部分 15 2.1 主要原料 15 2.2 主要仪器设备 15 2.3 试验方法 16 2.3.1 相图的绘制 16 2.3.2 电导率的测定 16 2.3.3 复合乳化剂微乳液法制备聚苯胺 16 HYPERLINK \l _TOC_250003 2.3.4 碳纸负载 PANI 电极的制备 16 2.4 性能测试与表征方法 16 2.4.1 产率的计算 16 2.4.2 聚苯胺电导率的测定 17 2.4.3 循环伏安测试 17 HYPERLINK \l _TOC_250002 2.4.4 Tafel 曲线的测试 17 HYPERLINK \l _TOC_250001 2.4.5 X 射线衍射分析(XRD) 17 HYPERLINK \l _TOC_250000 2.4.6 紫外-可见光谱分析(UV) 17 3 结果与讨论 18 3.1 磁场对复配乳化剂苯胺微乳液聚合体系相行为的影响 18 3.1.1 复配乳化剂微乳液体系的相行为 18 3.1.2 磁场对微乳液体系相行为的影响 21 3.1.3 磁场对微乳液体系电导行为的影响 22 3.1.4 有、无磁场条件下，复配乳化剂的配比对微乳液体系电导行为的影响 23 3.2 合成条件对聚苯胺性能的影响 24 3.2.1 复合乳化剂配比的选择 24 3.2.2 复合乳化剂的用量对聚苯胺性能的影响 25 3.2.3 复合乳化剂与单乳化剂微乳液法合成聚苯胺的性能比较 27 3.2.4 A