NdNi2Ge2化合物晶体结构和电磁性能.PDFVIP

The 7th National Conference on Functional Materials and Applications   Structure and Electromagnetic Properties of NdNi Ge 2 2 Hong-fei Yu, Yong-quan Guo, Xiao-hui Wu, Lu-shan Zhang School of Energy Power and Mechanical Engineering, North China Electric Power University, Beijing, China，102206 Email: yuhongfei@ncepu.edu.cn, Zhuxinzhuang, Dewai, Beijing, P.R.China Abstract: The structure of alloy NdNi Ge has been investigated using X-ray diffraction, TREOR and 2 2 Diamond. It is shown that this alloy crystallizes a tetragonal structure with space group of I4/mmm and its lattice parameter is a=4.1219Å，c=9.8366Å. The field dependence of magnetization curve is measured with an applied field of 5000Gs in cooling magnetic field model. The measurement shows this intermetallic compound is paramagnetic with a Curie-Weiss Constant of 25.8 and Curie-Weiss Temperature of 6.24K. The effective magnetic moment is 3.69μB. The variation range of resistivity is 0.3Ω·μm～1.1Ω·μm under the temperature range of 25 K～250K and indicated the compound semi-metal. Keywords ：structure; electromagnetic properties; NdNi Ge 2 2 NdNi Ge 化合物的晶体结构和电磁性能 2 2 于洪飞，郭永权，吴小会，张鲁山 能源动力与机械工程学院，华北电力大学，北京，中国，102206 Email: yuhongfei@ncepu.edu.cn, 中国北京德外朱辛庄 摘 要：本文应用X 射线衍射，TREOR 和Diamond 软件方法分析了NdNi Ge 化合物的相结构。研究 2 2 结果表明该化合