dl05电缆钢导电率的影响因素研究-冶金工程专业毕论文.docxVIP

AbstractWith Abstract With the gradual deepening of China’S modernization construction，gross domestic product(GDP)has jumped to the second place in the world，the skills change rapidly in manufacturing areas，SO the user’S demands are higher and higher to the iron and steel products’quality and performance as one of the necessary raw materials，DL05 cable steel produced by a steel plant is a typical product with quality performance guaranteed。 Therefore，there are important theoretical significance and practical application value to do the further study on the conductive mechanism of DL05 cable steel、the relationship between chemical composition、grain size and electrical conductivity for DL05 cable steel electrical conductivity’S assurance and improvement。 The results of thermal simulation experiment show that the microstructure obtaining after cooling don’t depend on the cooling speed，the ferrite structure Can be obtained under various cooling rate，and the grade of grain size is almost the same。In order to get better structure，the cooling rate of the steel should be 1-3。C／s，it provides the basis for establishing controlled cooling processes。 Based on the data measured in production scene，the research results that there is a direct relationship between electrical conductivity and chemical composition by analyzing the data。Data analysis shows that the higher w∑总、w∑(c、sj、P、s、N)、 w∑(Ni、Cr、Mo、c。)、w[Als]、w[Cu]、w[Mn]is，the lower electrical conductivity is， electrical conductivity is not associated with W， ，and manganese element has the most impact。 The smaller the grain size is，the bigger the grain is，the higher the electrical conductivity will be，and the grade of it is 6．0-8．5。Some parameter of hot working processes are chosen by the experiment and through experience，it is obtained that the optimum reheating procedure is 1 130-1210。C at heating zone and 1080——1 140。C at soaking zone。The ideal grain size could be obtained by rapid heating and short thermal insulation。 II