上胶剂对t800碳纤维表面的浸润性以及其复合材料界面性能yign的影响-材料工程专业毕业论文.docxVIP

北京化工大学硕士学位论文料耐热性和界面性能更明显：添加O．5wt％的Cationic 北京化工大学硕士学位论文 料耐热性和界面性能更明显：添加O．5wt％的Cationic CNC后T800．3碳纤 维／环氧828复合材料的界面层间剪切强度(IFSS)由114 MPa提高到 123MPa，Tg提高了4。C，因此在复合材料层间引入一定浓度的纤维素纳米 晶，能够增强复合材料的界面性能。 关键词：T800碳纤维，复合材料界面，上胶剂，热处理，纤维素 纳米晶，多尺度增强。 II 万方数据 AbstractThe Abstract The effect of sizing agent on the surface of T800 carbon fibers and the interphase properties of their composites Abstract The carbon fiber／resin matrix composites are widely used in the many fields．The interphase is composed of two parts that are between fiber and sizing agent and between sizing agent and matrix．The sizing agent can reacted with the surface of carbon fiber,which is the important role in the composites． First，this paper aimed to study the effect of heat treatment on the surface properties of T800 grade carbon fibers and the interface properties of carbon fibers reinforced epoxy composites．This paper investigated two different carbon fibers(T800-1，T800-2)，and the effect of sizing agents on the carbon fiber surface properties．Carbon fibers were heat-treated and then went through modifying to study the properties．The results of the study indicate that the heat treatment temperature of carbon fibers has an important influence to the carbon fibers composites due to the reactivity of sizing agent．This is due to different surface morphology,different amounts of functional groups， different kinds of sizing agent and different preparation conditions on T800-1 and T800．2 carbon fiber surface．Heat treatment contributes to the main enhancement of chemical interaction between T800．1 carbon fibers in the composites，while the trenches developed on the T800—2 can contribute to the physical interaction more． Second，this paper aims to study impact of coated different functionalized and contents of CNCs(cellulose nanocrystals)in the sizing agent(aq)on interfacial properties of T800 carbon fibers with epoxy(EP)resin matrix．Different functionalized and contents of cationic CNCs(cellulose 万方数据 北京化工大学硕士学位论文nano