镁合金表面化学镀镍 　　镁合金表面化学镀镍处理 　　摘要：本实验研究以硫酸镍为主盐的AZ91镁合金化学镀镍。选择适合的工艺流程、对实验材料进行化学镀镍处理、对化学镀镍层进行宏观或微观形貌观察、测量镀镍层的硬度、检验化学镀镍层的耐蚀性。实验表明，用该工艺能够在AZ91合金表面上生成化学镀镍层，镀层表面为胞状结构而且胞表面的晶界和缺陷较多，化学镀镍层较好地提高了镁合金的耐腐蚀性能，硬度有所提高。 　　　　关键词：AZ91D 镁合金 化学镀镍 腐蚀性 硬度 　　　　The chemical nickel plated of the surface of 　　Magnesium alloy 　　　　Abstract: The experimental study the nickel plating of Magnesium alloys of AZ91 that the sulfuric acid salt of nickel is the mainly electroless. Select the appropriate process, chemical nickel plating for experimental material, macro-or micro-morphology of electroless nickel deposits, measuring the hardness of nickel-plated, testing chemical corrosion resistance of nickel plating. Experiments show, we can generated plating layer on the surface of the AZ91 alloy with this technology, and the surface of the plating is the cell structure and there are more grain boundaries and defects on the cell surface ,the sulfuric processed chemical nickel plating layer is good to improve the magnesium alloy corrosion resistance, and the hardness is improved. 　　　　Keywords: AZ91D magnesium alloy electroless nickel plating corrosive hardness 　　　　t 　　　　目 录 　　第一章 绪论??????????????????????????1 　　1.1 镁合金概况???????????????????????1 　　1.2 化学镀镍概况??????????????????????1 　　第二章 实验过程????????????????????????3 　　2.1实验材料及设备?????????????????????3 　　2.2实验方法????????????????????????3 　　第三章 实验结果及分析 ????????????????????4 　　3.1金相分析????????????????????????4 　　3.2硬度分析????????????????????????7 　　3.3注意事项????????????????????????8 　　第四章 结论??????????????????????????9 参考文献 ???????????????????????????10 　　　　第一章 绪论 　　　　1.1 AZ91镁合金的概况 　　1.1.1镁合金 　　镁及其合金具有许多优良的物理和机械性能, 具有较高的比强度和比刚度、易于切削加工、易于铸造、减震性好、能承受较大的冲击震动负荷、导电导热性好、磁屏蔽性能优良, 是一种理想的现代结构材料 。为使镁合金应用于不同的场合, 经常需要改变其表面状态以提高耐蚀性、耐磨性、可焊性、装饰性等性能。目前有许多工艺可在镁及镁合金表面上形成涂覆层, 包括电镀、化学镀、转化膜 ,阳极氧化、氢化膜、有机涂层 、气相沉积层等。其中最为简单有效的方法就是通过电化学方法在基体上镀一层所需性能的金属或合金, 即电镀与化学镀。 　　1.1.2镁合金的腐蚀 　　化学腐蚀:镁合金的腐蚀实质上是镁被氧化成氧化镁或氢氧化镁的电化学和化学过程。从热力学角度看，不同价态的镁及其化合物的电化学位和自由能都要比单质镁低得多。由此可见，镁的腐蚀过程是自发的、极易发