阶梯型钢制零件冲压工艺分析及模具设计.docVIP

摘 要 拉深是利用模具使平板毛坯变成为开口的空心零件的冲压方法，用拉深工艺可以制成筒形、阶梯形、锥形、抛物面形、盒形和其他不规则形状的薄壁零件，其中又以筒形件简单和多见，而有凸缘筒形件又分为宽凸缘和窄凸缘件。 在拉深工艺设计时，必须知道冲压件能否一次拉出，这就引出了拉深系数的概念。拉伸系数决定于每次拉深时允许的极限变形程度。在多次拉深中，对于宽凸缘拉深件，则应在第一次拉深时，就拉成；零件所要求的凸缘直径，而在以后各次拉深中，凸缘直径保持不变。为了保证以后拉深时凸缘不变形，宽凸缘拉深件首次拉入凹模的材料应比零件最后拉深部分实际所需材料多3%~5%,这些多余材料在以后各次拉深中，逐渐将减少部分材料挤回到凸缘部分，使凸缘增厚，从而避免拉裂。 关键词：拉深；成型工艺；拉裂 Abstract The deep drawing is a pressing process. It can make a sheet blank into a uncork piece with die. A process with deep drawing can manufacture workpiece in many shapes. And the tappered workpiece which includes broad protruding edge workpieces and narrow protruding edge workpieces is the most usual. The coefficient of the deep drawing is important when you have to be sure whether it can make it in one time. The coefficient lies on the limit of the deformation degree every deep drawing process allows. Key words: deep drawing; forming process; restriction crack 目 录 TOC \o 1-3 \h \z \u HYPERLINK \l _Toc201066619 摘 要 PAGEREF _Toc201066619 \h I HYPERLINK \l _Toc201066620 Abstract PAGEREF _Toc201066620 \h II HYPERLINK \l _Toc201066621 1 绪论 PAGEREF _Toc201066621 \h 1 HYPERLINK \l _Toc201066622 2 拉深件的工艺性分析 PAGEREF _Toc201066622 \h 3 HYPERLINK \l _Toc201066623 2.1 分析工件的冲压工艺性 PAGEREF _Toc201066623 \h 3 HYPERLINK \l _Toc201066624 2.2.1 工件形状 PAGEREF _Toc201066624 \h 3 HYPERLINK \l _Toc201066625 2.2 08F材料的化学成分和机械性能 PAGEREF _Toc201066625 \h 4 HYPERLINK \l _Toc201066626 3 拉深工序计算 PAGEREF _Toc201066626 \h 5 HYPERLINK \l _Toc201066627 3.1 阶梯形筒形件的拉深工序计算原则 PAGEREF _Toc201066627 \h 5 HYPERLINK \l _Toc201066628 3.1.1 阶梯形件拉深工序计算程序 PAGEREF _Toc201066628 \h 5 HYPERLINK \l _Toc201066629 3.2 必要的工序计算 PAGEREF _Toc201066629 \h 5 HYPERLINK \l _Toc201066630 3.2.1 修边余量δ的确定 PAGEREF _Toc201066630 \h 5 HYPERLINK \l _Toc201066631 3.2.2 毛坯尺寸计算 PAGEREF _Toc201066631 \h 5 HYPERLINK \l _Toc201066632 3.2.3 判断阶梯筒形部分的拉深次数 PAGEREF _Toc201066632 \h 7 HYPERLINK \l _Toc201066633 3.2.4 确定工件的制造工序步骤 PAGEREF _Toc201066633 \h 8