激光熔覆原位合成TiC2fFeAl复合涂层分析.pdfVIP

摘要 接率为40% ）失重明显低于单道熔覆层，耐磨性能更好，这是由于多道搭接降低熔池母 材对熔覆层的稀释作用，减弱了熔覆粉末向母材的扩散以及被固溶，原位合成TiC 增多， 硬质增强相之间的距离进一步减小，更有利于承载和抗磨。 关键词：激光熔覆，TiC/FeAl 原位复合涂层，热力学，动力学，耐磨性，硬度 II 万方数据 Abstract STUDY ON IN-SITU SYNTHESIS TIC/FEAL COATING BY LASER CLADDING ABSTRACT The traditional steel parts often cause great economic loss in commercial app lication due to surface abrasion.The method of preparing high hardness and wear resistant coatings on the surfaee of part s is an important way to prolong the part s’ life and rep air the failure partsof machinery. In the presents tudy, TiC ceramics particles enhanced FeAl matrix cladding layer was prepared by laser cladding in-situ synthesized in the form of coaxial powder feeding on the surface of Q235 steel. By means of differential scanning calorimeters(DSC) and X-ray Diffractometer(XRD), the thermodynamics and kinetics of the synthetical reactions in Fe-Al- Ti-C system were analyzed; the reaction thermodynamics of the cladding powder system were researched, and the kinetic model for the in situ TiC/FeAl composite coating made through the laser cladding technique was formulated.M acro morphology, microstructure and worn surface mropologies of coatings were analyzed and characterized by optical microscope and scanning electron microscopy, phase composition was analyzed by energy dispersive spectrometer and X-ray diffraction. The hardness and wear resistance were test respectively by microhardness tester and wear testing machine.The reinforc ed mechanism and