镍纳米纤维与镍纳米颗粒的制备和性能表征.pdfVIP

NiO powders by calcining precursor xerogel in air , (3) reduction by hydrogen into Ni powders. In this paper, the content of the citric acid had positive effects on grain size of Ni nanoparticles, the grain size were decrease with the content of the citric acid. The magnetic property was measured by VSM, The saturation magnetization, coercivity and remanent magnetization of the obtained Ni nano fibers was 75.3Oe to185Oe, 46.3emu/g to 51.9emu/g and 7.9 to 16.9emu/g, respectively. The samples appeared magnetic agglomeration due to the great