基于csp工艺取向硅钢抑制剂及初次再结晶行为的研究-材料工程专业论文.docxVIP

内蒙古科技 内蒙古科技大学硕士学位论文 quantitative analysis. This study about primary recrystallization behavior on different decarburization annealing process has certain guiding significance. The results of the study show that: before the primary recrystallization annealing, there are obvious differences of normalizing grain size, the textures distribute random. There are more precipitations on the microstructure, and there are some differences between the size of precipitation and precipitation distribution. At the same time, MnS and AlN precipitations precipitated by the micro alloy form. After primary recrystallization annealing, the grain refined, decarburizing annealing samples which holding time is 5 minute in 840℃ have smaller primary recrystallization grain size,the character of Grain boundary is ideal. Among them, high-energy grain boundary Σ3 and Σ9 enrich at grain boundaries around the favorable orientation, it is promoting the formation of favorable orientation. With prolonging annealing time, large angle boundaries and favorable orientation of declining numbers are not conducive to the nucleation and growth of Goss grain. After primary recrystallization annealing process of decarbonization, the overall precipitates are distributed in dispersion state. The percentage content of MnS and AlN precipitations in normalized plate and primary recrystallization annealing samples are constantly increasing.Under the different process of primary recrystallization, precipitated phase has the highest percentage with holding 5 minute.Compared with the corresponding precipitation morphology, the effect is obvious. Key Words：Oriented silicon steel；Compact strip production (CSP)；The primary recrystallization；Inhibitor III PAGE PAGE 1 目 录 摘 要 I Abstract II 引 言 1 1 文献综述2 1.1 取向硅钢简介2 1.2 取向硅钢的需求及其发展趋势3 1.2.1 国外取向硅钢的发展趋势3 1.2.2 国内取向硅钢的发展趋势6 1.2.3 取向硅钢的未来发展趋势8 1.3 取向硅钢产品性能的影响因素9 1.3.1 微量合金元素对取向硅钢性能的影响9 1.3.2 晶粒尺寸对取向硅钢性能的影响 10 1.3.3 抑制剂在取向硅钢生产过