万方数据 万方数据 摘要摘 摘要 摘 要 本课题针对冻结法凿井施工后期冻结管解冻极易形成导水泌道这一现象，研 究用冻结盐水来配置水泥浆进行封填。要求该水泥浆要满足抗冻性、比重、强度、 凝结时间等方面的要求。 研究结果表明：通过研究，发现用冻结盐水配置的水泥浆满足抗冻性要求。 采用多组不同水灰比水泥浆的对比实验，发现水灰比越高的水泥浆的比重也越 高，水灰比越高的水泥浆其相应的强度反而越低。通过模型实验，发现当水泥浆 的比重在1．6一1．7时，其施工效果最佳。此外，还通过对初凝时间，终凝时间等 的研究，发现水灰比在0．8-0．9之间的水泥浆最佳，最适合用作封填材料。 通过实验和模型实验的研究，我们找到了最佳水灰比的冻结盐水配置的水泥 浆。最后，还应进行现场实验。冻结法凿井深冻结管充填新材料的研究还要继续， 因此在以后的施工实践以及科学研究过程中，还要去研究新的材料，要求新材料 更能满足实际施工的需要，更能保证实际施工的质量。并且还能在更多的功能领 域有所拓展，如节能，耐腐蚀等，以实现性能功能与环境相统一。 图[56]表[9] 参[63] 关键词：冻结法凿井；深冻结管；充填新材料：施工工艺 分类号：TD262 II AbstractAbstract Abstract Abstract Research topic of this thesis：Since the freeze thaw holes can easily form a water guide channel secretion，the researchers use to configure certain mine brine water-cement ratio and the proportion of grout sealing fill．Require the slurry has the following characteristics：resistance，the requirements of specific gravity，the strength． The results show that：the study found that wim mine brine slurry configured to meet the requirements for frost resistance．Using different sets of water-cement ratio of cement slurry comparative experiments，we found water-cement ratio，the higher the proportion of the higher grout，grout cement ratio，the higher the corresponding strength but lower．Through model experiment，found that when the proportion of 1．6-1．7 grout，its construction best．In addition，through the study of the initial setting time and final seRing time was found in the water-cement ratio of between 0．7—0．8 grout the best and most suitable for use as sealing filler material． Through research experiments and model experiments，we found the best water-cement ratio of ore slurry with brine configuration．Finally,field tria ls should be carried out．Study freezing sinking deep freeze hole fill the new material will continue SO in the future construction practices and scientific process，but also to study new materials require new materials to better meet the needs of the actual construction，better ensure that the actual quality of construction．And