电子束焊接热冲击对GH4133A的微裂纹损伤研究.PDF

36 / 2001 2 4133 GH A Study on M icrofissuring Damage of Ni-base Superalloy - under T hermal Shoc of Electron beam Welding 1 1 1 2 3 , , , , ( 1 , 100083; 2 , 100095; 3 , 100024) 1 1 1 2 3 ZHANG Hai-quan , ZHANG Yan-hua , Li Liu-he , ZHANG Xing-an , MA Xiang-sheng ( 1 Beijing University of Aeronautics and Astronautics, Beijing 100083, China; 2 Institute of Aeronautical Materials, Beijing 100095, China; 3 Beijing Aeronautical M anufacturing Technology Research Institute, Beijing 100024, China) : , , GH4 133A , , : ; ; ; : T G402; O346. 5: A : 1001-4381 ( 2001) 02-0036-04 : ( ) Abstract Electron beam welding EBW process is a complicated and violent instantaneous thermal shoc process that consists of a thermal process occurred on the weldment surface and interactional mechanical process existed betw een the stress w ave and base metal in certain depth The reason of. - ( ) heat affected zone HAZ microfissuring presented in superalloy EBW joints was analyzed based on . thermal shoc effect The influence of microfissuring damage on high temperature mechanical prop- . erties of EBW joints w ere also discussed T he results show that the HAZ microfissuring damage of superalloy EBW joints induces mechanical properties deterioration w hich is attributed to the EBW thermal shoc . Key words: electron-beam w elding; thermal shoc ; HAZ microfissuring; damage effect , , , , ,