磺化聚苯胺性能的研究3.PDF

华南师范大学学报 ( 自然科学版) 2002 年 5 月 　　　　　JOURNAL OF SOUTH CHINA NORMAL UNIVERSITY 2002 年第 2 期 May 2002 　　　　　　 (NATURAL SCIENCE EDITION) 　　　　　　 　No . 2 , 2002 : ( ) 文章编号 1000 - 5463 2002 02 - 0089 - 04 磺化聚苯胺性能的研究 于黄中 , 刘少琼 , 黄 　河 , 熊予莹 (华南师范大学物理学系 , 广东广州 5130160) 关键词 : 聚苯胺 ; 磺化聚苯胺 ; 发烟硫酸 中图分类号 : TN304 . 52 　　　　文献标识码 : A PROPERTY STUDY ON THE SUL FONATED POLYANIL INE YU Huang - zhong , LIU Shao - qiong , HUAN G He , XION G Yu - ying (Department of Physics , South China Normal University , Guangzhou 510631 ,China) Abstract : Using 30 % fuming sulfuric acid to sulfonate emeraldine base ( EB ) , sulfonated polyaniline ( SPAN) is synthesized . The results show that it has higher solubility and good con ductivity , and SPAN with different sulfonation degree ( SD) possesses different conductivity . With the increase in SD of the SPAN , its conductivity (σ) decreases but its solubility is im proved . UV - Vis spectra indicate that SPAN has a red shift compared with PANI. The colloid aggregates and loose structure have been found by using TEM. Key words : polyaniline (PANI) ; sulfonated polyaniline ( SPAN) ; fuming sulfuric acid 　　本文利用 30 %发烟硫酸磺化聚苯胺 ,聚苯胺经发烟硫酸磺化后 ,在其苯环上带上磺酸基 团 - SO3 - . 由于苯环侧链上磺酸基团 - SO3 - 的引入 ,使得聚苯胺的溶解性能、导电等性能得到 改善 ,并讨论了磺化后聚苯胺性质的变化. 1 　实验部分 11 　本征态聚苯胺( PANI) 的合成 将含 11. 5 g 和过硫酸胺的 1 mol 盐酸溶液缓慢加入到预冷到 0 - 4 ℃的装有经 2 次减压蒸 馏的分析纯苯胺单体 9 . 4 mL 和 200 mL 1 mol 盐酸的三口瓶中 ,在冰浴连续反应 5 - 6 h ,溶液为 墨绿色 ,过滤 ,依次用 1 mol/ L 盐酸 、蒸馏水洗涤. 再用丙酮抽提 ,在 80 ℃真空烘箱中干燥 10 h . 用质量分数为 3 % NH OH 处理 24 h ,得到本征态 PANI. 4 收稿 日期 : 2001 - 05 - 15