建筑垃圾资源化制备再生骨料混凝土的研究-材料学(无机材料)专业论文.docx

暨南大学硕士学位论文 暨南大学硕士学位论文 II II 作性能、力学强度和耐久性能均要好于一次再生粗骨料混凝土；利用二次再生粗骨料制备 高强再生粗骨料混凝土，所制备的二次再生粗骨料混凝土的工作性能和耐久性能要好于一 次再生粗骨料混凝土，但是力学强度要低于一次再生粗骨料混凝土。 （8）含有多种成分的建筑垃圾资源化利用制备再生骨料混凝土是可行的，且再生粗骨 料的多次循环利用制备再生粗骨料混凝土也是可行的。 关键词：建筑垃圾；再生骨料；再生混凝土；稻壳灰；再生微粉 III III ABSTRACT In our country, urban construction waste production has increased with Urbanization. It’s reasonable resource utilization for these “urban mining” has achieved everyone’s consensus. At present, there are a lot of researches and applications on the recycled aggregate concrete produced by recycled concrete aggregates, and the waste concrete was sorted out from the construction waste and then processed into recycled concrete aggregates. However, in the actual process, construction waste sorting is more difficult and requires relatively high cost. In view to this situation, we chose the construction waste as the research object, which contains a variety of compositions, such as waste concrete, waste brick, waste mortar, waste ceramic and waste glass. In order to help the actual production, the construction waste recycled aggregates and its preparation of recycled aggregate concrete were systematically studied. The following conclusions were drawn from these works: When the coarse aggregate concrete and fine aggregate concrete designed strength grade was C30.The maximum replacement ratio of recycled coarse aggregates was 50% in the recycled coarse aggregate concrete and recycled fine aggregates was 20% in the recycled fine aggregate concrete. he performance of recycled aggregate concrete which was prepared by 50% recycled coarse aggregates and 20% recycled fine aggregates were lower than the recycled aggregate concrete, which was prepared by 50% recycled coarse aggregates or 20% recycled fine aggregates. To compare with the normal concrete, it’s 28d compressive strength was reduced by 28.9%, wear loss was higher than 0.305g/cm2, compressive strength loss rate was higher than 4.9% and splitting tensile strenrth loss rate was hi