CO2气体保护焊短路过渡熔滴尺寸的研究.PDFVIP

CO 气体保护焊短路过渡熔滴尺寸的研究 2 太原科技大学 齐志龙，李 科，孙佳男，吴志生 （材料科学与工程学院 山西 太原 030024 ）  （期刊名称：焊接，出版时间：2016.11） 指导教师：吴志生 教授 摘 要： 利用高速摄影系统拍摄了 CO 气体保护焊熔滴过渡过程，借助高速摄影图像，通过椭球-球转换法精确测量了 2 短路时的熔滴尺寸，分析了焊接电流、焊接电压、焊丝伸出长度和焊接速度对熔滴尺寸的影响。结果表明，熔滴尺寸与焊接 电流成反比，与焊接电压成正比，随着焊丝伸出长度的增加，熔滴尺寸先减小后增大，在可焊的范围内，焊接速度几乎不影 响熔滴尺寸。研究结果可为精确控制熔滴尺寸、提高焊接质量提供参考。 Abstract: With the help of a high-speed photography system, the droplet transfer process of CO gas shielded arc welding was 2 filmed. Based on the high-speed images, the droplet size at the moment of short-circuit was accurately measured by ellipsoid-sphere conversion method, and the effects of welding current, welding voltage, wire extension and welding speed on droplet size were analyzed. The results show that, the droplet size is inversely proportional to welding current and proportional to welding voltage, with the increase of the length of wire extension, the droplet size decreases first and increases later, within the allowable welding range, welding speed hardly affects the droplet size. It provides a reference for precisely controlling droplet size and improving weld quality. 关键词：CO 气体保护焊；短路过渡；熔滴尺寸；高速摄影 2 CO2 气体保护焊的短路过渡具有低成本、低热输入、高效率的特点，在低碳钢和低合金钢结构件的薄 [1] 板和中厚板焊接中得到了广泛的应用 。但短路过渡时的飞溅率大，焊缝成形质量较差，导致焊材及能量 利用率降低。如何在高的熔敷速度下解决短路过渡焊接时的飞溅问题一直是困扰工业界的难题和焊接学术 领域的研究热点[2-4] ，而分析短路过渡熔滴尺寸的影响因素及其变化规律对有效控制熔滴尺寸及改善焊接工 艺性能具有重要意义。 [5] 早期对于熔滴尺寸的测量主要采用熔滴收集法，包括水冷收集法和干法收集 ，由于收集到的熔滴并 不是沿着电弧区域落入熔池，而是脱离电