铝合金型材挤压过程的数值模拟研究-材料工程专业毕业论文.docxVIP

江西 江西理工大学硕士学位论文 Abstract PAGE PAGE III parameters of the extrusion is that the billet diameter is 205 mm, the extrusion speed is 3.2 mm/s, the preheat temperature of the billet is 480 ℃, the preheat temperature of extrusion die is 470 ℃, the preheat temperature of the container 440 ℃. For the index parameters of the ram force, the billet diameter is 200 mm, the extrusion speed is 1.4mm/s; the preheat temperature of the billet is 490 ℃, the preheat temperature of extrusion die is 480 ℃, the preheat temperature of the container 460 ℃. (4) The effect of software Hyperxtrude on the extrusion process rule was proved correctly, comparing proximate product with software Hyperxtrude simulation and actual extrusion. Keywords: aluminum profile; extrusion process; extrusion die; extrusion process parameters; numerical simulation 江西 江西理工大学硕士学位论文 目录 PAGE PAGE IV 目 录 摘 要 I AbstractII 目 录 IV 第一章 绪论1 1.1 引言1 1.2 铝合金型材挤压成型技术2 1.2.1 挤压的基本原理及特点2 1.2.2 铝型材挤压挤压过程及金属流动特性3 1.2.3 挤压制品常见挤压缺陷及产生原因4 1.3 铝合金型材挤压的研究方法6 1.3.1 理论解析法6 1.3.2 数值分析法7 1.4 本次课题研究背景7 1.5 本次课题研究内容概述8 1.6 本次课题研究方案思路简述9 第二章 铝合金型材挤压模具设计 11 2.1 引言 11 2.2 铝型材挤压模具简介 11 2.2.1 挤压模具的常见类型 11 2.2.2 挤压模具材料选择13 2.3 挤压筒、挤压坯料以及挤压模具形状确定原则14 2.4 平面分流组合模具设计15 2.4.1 分流组合模具加工简介15 2.4.2 分流组合模结构设计15 2.5 本章小结18 第三章 挤压铝合金型材过程数值模拟原理19 PAGE PAGE VI 3.1 引言19 TOC \o 1-2 \h \z \u HYPERLINK \l _TOC_250007 3.2 ALE 法的基本理论 19 HYPERLINK \l _TOC_250006 3.2.1 ALE 法的基本概念以及描述方法 19 HYPERLINK \l _TOC_250005 3.2.2 ALE 算法的基本控制方程 20 HYPERLINK \l _TOC_250004 3.2.3 ALE 算法在不可压缩流体稳态流动的描述 21 HYPERLINK \l _TOC_250003 Altair hyperxtrude 软件简介 24 HYPERLINK \l _TOC_250002 Hyperxtrude 软件的功能 24 HYPERLINK \l _TOC_250001 Hyperxtrude 软件模拟流程 25 HYPERLINK \l _TOC_250000 Hyperxtrude 收敛准则 25 第四章 模具结构参数对铝合金型材挤压过程的影响研究27 4.1 引言27 4.2 挤压模具建立27 4.3 挤压模型和模拟设置28 4.3.1 高温下铝合金材料模型28 4.3.2 挤压摩擦模型30 4.3.4 模拟边界条件设置30 4.3.5 挤压模拟前处理网格划分31 4.3.6 模拟计算参数设定32 4.4 正交试验方案确定33 4.5 正交试验结果及分析35 4.5.1 试验模拟结果35 4.5.2 实验结果直观分析36 4.6 综合指标分析39 4.7 试验验证