锂离子电池钛酸锂负极材料的制备及电化学性能研究-化学工程专业论文.docxVIP

重庆大学硕士学位论文 重庆大学硕士学位论文 英文摘要 PAGE PAGE IV temperature, hydrothermal time and sintering temperature on performance and morphology of sample were investigated. The results indicated that the pure spinel lithium titanate was prepared when 10mmol tetrabutyl titanate reacted with 9mmol lithium hydroxide; When the hydrothermal temperature was lower than 170℃, the impurity phase of TiO2 appeared in the sample; when the hydrothermal temperature was 170℃, the pure spinel phase was prepared. The hydrothermal reaction time has a great influence on the morphology of the as-synthesized products. When the