中国资源综合利用 Vol.36，No.6 试验研究 China Resources Comprehensive Utilization 2018年6月 超细粉煤灰的特性研究 仪桂兰 （山西太钢不锈钢股份有限公司，太原  030003） 摘要：为激发粉煤灰的活性，提高粉煤灰的利用率，本文对粉煤灰和超细粉煤灰的粒度分布、化学组成、 物相组成、颗粒形貌以及活性等基本特性进行了研究。同时，通过差热分析研究了超细粉煤灰活性增强的 机理。结果表明，粉煤灰经超细加工后，其晶体结构有一定程度的无定形化，晶体相衍射峰强度降低，超 细粉煤灰活性较好。 关键词：粉煤灰；超细粉煤灰；基本特性；活性 中图分类号：TU528.041 文献标识码：A 文章编号：1008-9500(2018)06-0032-06 Research on Basic Property of Fly Ash Yi Guilan (Shanxi Taigang Stainless Steel Co., Ltd., Taiyuan 030003, China) Abstracts: In order to stimulate the activity of fly ash and improve the utilization of fly ash, this paper studied the particle size distribution, chemical composition, phase composition, particle morphology and activity of fly ash and ultrafine fly ash. At the same time, the mechanism of the activity enhancement of ultrafine fly ash was studied by differential thermal analysis. The results show that after superfine processing of fly ash, the crystal structure has a certain degree of amorphization, the diffraction peak intensity of crystal phase decreases, and the activity of ultrafine fly ash is better. Keywords: fly ash; ultrafine fly ash; basic property; activities 粉煤灰可作为掺合料用于水泥混凝土行业，但 1.2 粉煤灰成分 部分粒度较粗的粉煤灰由于活性较低，不能直接用作 1.2.1 粉煤灰成分 水泥混合材、高性能混凝土的活性掺合料，使粉煤灰 原灰以及不同粒度粉煤灰的成分如表 2 所示。 在利用上受到了很大的限制。为激发粉煤灰的活性， 由 表 2 可 知， 粉 煤 灰 的 主 要 成 分 是 SiO2 和 提高粉煤灰的利用率，本文主要研究粉煤灰及超细粉 Al O ，二者大约占 85%。而且，不同粒度的粉煤灰 2 3