建筑行业期刊：低品质粉煤灰在混凝土中的应用研究.pdfVIP

doi-1 O．39694 issn．1 671—91 07．201 5．09．057 低品质粉煤灰在混凝土中的应用研究 Study on Application ofFly Ash ofLow Quality in Concrete 刘围’，丁华柱 ，都增延。，黄贤德 (1重庆市东毅新型建材有限公司，重庆 401334；2重庆筑能建材有限公司，重庆 400713； 摘要：该文研究了低品质粉煤灰的活性指数和其对胶砂流动度和混凝土各项性能的影响。结果表明：低品质粉煤灰的活性指数随着其细度的增 加而增加．但增加趋势逐渐放缓；掺入低品质粉煤灰的胶砂流动度随着细度的增加呈现先增大后减少的趋势；低品质粉煤灰能够满足混凝土的 各项性能．所以能够在工程应用中大量使用 关键字：低品质粉煤灰；活性指数；流动度；混凝土 中图分类号：TU528 文献标识码：A 文章编号：1671—9107(2015)09-0057-03 Abstract：This paper studies the activity index of flash of low qu~ity with its impa~011 fluidity of mortar and on the prope~ies of concrete．The results show that the activity index of low quality fly ash increases with the increase of its fitness，but the increase trend is steadily slowed down，and that the fluidity ofmortar mixed with low quality fly ash firstly increases and then decreases with the increase offimess．SO it call be widely used in the engineer- ing application for its capability ofmeeting the various properties ofconcrete． Key words：fly ash oflow quality；activity index；fluidity；concrete 1．1．1水泥 0引言 试验选用重庆拉法基水泥有限公司生产的拉法基普通 42．5R水泥，其化学成分见表1。 随着我国建筑行业飞速发展．对矿物掺合料的利用已经 表1水泥的化学成分 向环保、经济的趋势发展．粉煤灰作为一种优质矿物掺合料的 综合利用不仅可以保护环境．还可以产生良好的社会经济效 益I1_ 粉煤灰是一种高分散度的人工火山灰质材料．主要化学 成分是二氧化硅、三氧化铝和三氧化二铁，另外还含有未燃尽 的碳粒、氧化钙和少量的氧化镁、三氧化硫等等[2-3]，其颗粒呈 1．1．2粉煤灰 多孔性蜂窝状组织．比表面积较大．具有较高吸附活性[41。我国 试验使用的粉煤灰是中石化四川维尼纶厂提供的粉煤 粉煤灰的密度和国外学者研究的粉煤灰密度略有差异．我国 灰，分别粉磨2min、10min、18min、30min后得到四种不同比表 粉煤灰的密度大致在1．77 2．43g／em3~E右．而国外粉煤灰密度 面积(350m2／kg、400m2／kg、450m2／kg、500m2／kg)的粉煤灰。粉煤 普遍比中国粉煤灰密度高嘲 灰的化学成分见表2。 粉煤灰根据细度、需水量比和烧失量分为三个等级．即 I 表2粉煤灰的主要化学成分 级粉煤灰、Ⅱ级粉煤灰和Ⅲ级粉煤灰。粉煤灰作为矿物掺合料 如今已广泛应用于土木建筑的混凝土结构中 粉煤灰用在土 木建