粒状陶瓷纤维浇注料.docVIP

PAGE PAGE ５ 粒状陶瓷纤维浇注料 grain ceramic fiber refractory castable 张克铭 鞍山市汇铭科技工程有限责任公司 鞍山 114001 Anshan Huiming Scientific Technology and Engineering.CD.LTD 摘 要 介绍了一种新型陶瓷纤维浇注料,将陶瓷纤维棉制成高强度的球柱状纤维颗粒，然后再用这种纤维颗粒置换耐火浇注料中的骨料而制成的粒状陶瓷纤维浇注料。它集重质耐火浇注料和轻质隔热浇注料的优点于一体,既具备强度高、耐高温的性能,又具备低体积密度、低导热率的隔热性能。 Summary Introduces a kind of new castable ceramic fiber, first it make the ceramic fiber cotton into the ball(pillar) form fiber grain,.then with this kind of fiber grain displacement the bone of material in refractory castable and forming the grain ceramic fiber refractory castable..It gathers the heavy quality refractory castable and the light quality partition heat castable advantage that in the whole body..Since have the strength high,bear the function of the heat,have the low physical volume density again,low transmit heat of the rate in partition heat. 关键词: 粒状陶瓷纤维，浇注料，隔热，高强度，低热导率 Key words: Ceramic fiber grain Refractory castable heat insuleis Strength high, Low transmit heat of the rate 前言 到目前为止，不论是国内还是国外研制生产的陶瓷纤维浇注料，其工艺过程基本上是：将陶瓷纤维棉破碎后直接掺入各种不定型耐火散料中。根据耐火度的不同，来选用不同种类的基质料和结合剂，将破碎后的陶瓷纤维加在这些散状料中。经搅拌、加水（加水量达到了40-90%其收缩大）和浇注成型后，破碎的陶瓷纤维分散度不好，大多都以云片状或团絮状大小不均匀的形式存在。虽然陶瓷纤维浇注料轻型隔热，但是浇注料的强度很低，收缩很大，并且也没真正发挥陶瓷纤维隔热的全部特性，也就是说，陶瓷纤维在与耐火散状料混合后纤维的多孔性能大多被破坏，多处被耐火泥浆灌满。一种材料在制品中分布所呈现的形体，直接影响到这个产品的整体强度和最佳隔热效果． 粒状陶瓷纤维浇注料，既具备了重质耐火浇注料的耐高温、高强度和高温下的低收缩率，又具备了轻质隔热浇注料的低导热率和高抗热震性。粒状陶瓷纤维浇注料导热系数500℃时0.48w/m.k左右。高强轻质浇注料的出现，改善了炉墙整体浇注的保温绝热效果，但大多轻质隔热浇注料其使用温度低，强度小。目前的氧化铝空心球耐火浇注料和莫来石高强轻质浇注料在110℃烘干的耐压强度虽然达到12－18Mpa，在高温下却提高很小，仅在25MPa，其导热系数在500℃时却＞0.8w/m.k，仍然比粒状陶瓷纤维浇注料导热系数大一倍左右 2.粒状陶瓷纤维浇注料热过程特性 2．1基本理化指标 　粒状陶瓷纤维浇注料基本理化指标见表1，指标来自标准试块（160mm×40mm×40mm，导热系数分别采用了热线法和平板法）近50块的数据统计平均结果， 　　　　　　　　　　粒状陶瓷纤维浇注料各项指标 表1 检 测 内 容 HM-2.0 HM-1.9 HK-1.8 AL2O3 % ＞65 ＞60 ＞60 耐压强度　Mpa 110℃×24h 12 10 1610 耐压强度　Mpa 1400℃×3h 35 32 32 抗折强度　Mpa 1400℃×3h 8.5 7.8 7 体积密度　g/cm3 2.0 1.88 1.85 线收缩率 % 1400 ＋0.11 －0.12 －0.14 导热系数 w/m.k 500℃ 0.