超疏水钛合金表面的制备及其摩擦学性能-中国有色金属学报.pdf

25 9 2015 9 Volume 25 Number 9 The Chinese Journal of Nonferrous Metals Sep. 2015 1004-0609(2015)-09-2421-07 ( 116026) Ti6Al4V 100 μm SiO2 (UMT)LEXT OLS4000 3D SiO2 Ti6Al4V 32.3% 53.8% Ti6Al4V TG146.2 A Preparation of super hydrophobic titanium alloy surface and its tribological performance LIAN Feng, REN Hong-mei, GUAN Shan-kun, ZHANG Hui-chen (College of Transportation Equipment and Ocean Engineering, Dalian Maritime University, Dalian 116026, China) Abstract: In order to study the impacts of the surface pattern and wettability on tribological performance, the laser processing was used to prepare grid and dot micro-structure with spacing of 100 μm on Ti6Al4V alloy surface. The SiO2 nano particles were coated on the micro-structures to build micro-nano structures. The contact angles and roll angles were measured by contact angle measurement. The tribological performance was evaluated by universal micro-tribometer(UMT). The micrograph and wear tracks were investigated by LEXT OLS4000 3D laser scanning confocal microscopy. The results show that the super hydrophobic Ti6Al4V surfaces with the micro-nano structure can be prepared by coating the SiO2 nano particles on the micro-structures. The grid surface is more difficult to be wet than dot surface. The harder the surface is wet, the lower the wear rate of sample is. The wear rates of super hydrophobic surface with dot and grid decrease by 32.3% and 53.8%,