镀铬以及予应力处理后对25Cr2Ni4WA30CrMnSiA-重庆义扬机电设备.doc

PAGE PAGE 4 镀铬以及予应力处理后对25Cr2Ni4WA、30CrMnSiA、 30CrMnMoTiA三种钢的缺口慢拉伸强度、含氢量的研究* 李志义 重庆义扬机电设备有限公司 摘要 通过试验，评价了25Cr2Ni4WA、30CrMnSiA、30CrMnMoTiA三种中碳高强度钢，在进行镀铬或予应力下镀铬，其镀铬工艺上限或上限条件下：渗氢量和缺口慢拉伸强度的影响。 采用常规的180℃× 关键词：镀铬，予应力处理，缺口慢拉伸强度， 含氢量，中碳高强度钢 Research of notch slowly tensile strength and quantities of Hydrogen in three different steels 25Cr2Ni4WA, 30CrMnSiA, 30CrMnMoTiA after Chromate treatment and pre-stress treatment Li Zhiyi1 Abstract In this paper, the effects of quantities of Hydrogen and notch slowly tensile strength have been evaluated in three different medium carbon high strength steels 25Cr2Ni4WA, 30CrMnSiA, 30CrMnMoTiA, by Chromate treatment or pre-stress Chromate treatment and with upper limit or low limit Chromate treatment process. The Hydrogen could not be eliminated absolutely by the ordinary dehydrogenation process 180℃×2h. The quantities of residual Hydrogen in center of the Chromate treated steels are 36% to 170% higher Key words: Chromate treatment, pre-stress treatment, notch slowly tensile strength, quantity of Hydrogen, medium carbon high strength steel 前言： 镀铬是常用的表面处理工艺，镀铬过程必然引起渗氢、氢脆，衡量氢脆的常用方法为含氢量和慢拉伸强度，而且这两个指标并不总是对应的关系。 对中碳合金钢、高强度钢的缺口慢拉伸强度、含氢量关系如何？目前国内暂无人问津。 为此我们选择25Cr2Ni4WA、30CrMnSiA、30CrMnMoTiA三种常用中碳合金高强度钢在常用的热处理条件下、进行镀铬以及应力镀铬。镀铬工艺上限或下限条件下，含氢量和慢拉伸强度试验，并进行断口的形貌观察。 采用常规的180℃× 试验条件： 2.1试验用材料及其化学成份： The chemical composition (wt%) of the test material 25Cr2Ni4WA C 0.235%， Si 0.27%， Mn 0.39%， P 0.013%， S 0.006%， Cr 1.15%， Ni 4.18%， Mo 0.04%， W 0.86%， Cu 0.18%； 30CrMnSiA C 0.29%， Si 1.07%， Mn 0.86%， P 0.013%， S 0.015%， Ni 0.10%， Cu 0.12%； 30CrMnMoTiA C 0.30%， Si 0.30%， Mn 0.98%， P 0.30%， S 0.011%， Cr 1.12%， * *注：该试验工作由中科院沈金所王毓麟研究员、李宪文、杜金山高工以及清华大学顾家琳教授（1985～1992）承担主要试验工作，特表感谢。 Mo 0.22%， Ti 0.085%. 作者简介：李志义（1938.2.1）男，江苏泰州人，汉族，1962年哈工大毕业，1992年由22个一级学会联合召开的 作者简介：李志义（1938.2.1）男，江苏泰州人，汉族，1962年哈工大毕业，1992年由22个一级学会联合召开的“全国机电装备失效分析预测防战略研讨会”授予全国先进失效分析专家称号，获国家发明专利一项又批准一项，获兵器部二、三等奖，已发表论文20多篇。著有：结构钢在表面处理过程中的氢脆和应力腐蚀断裂 [