一体成形电感用软磁粉末绝缘失效的研究.pdfVIP

Study on the Causes of the Failure of the Insulation Resistance of Molded Inductors with Soft Magnetic Materials 1 1 2 Guo Feng ; Li wei-jian ; Yan liang-ming 1：Global Vision Trading Ltd Kunshan City, Jiangsu Province, China, 2 ：Inner Mongolia University of Technology Material Science and Engineering institute, Hohhot, China Email address bruce_guo@ （GUOfeng ）；lwjv587@163.com （Li wei-jian ） （Yan liang-ming ） Abstract ：In this paper, the cause of the insulation resistance of molded inductor in low temperature baking is discussed, and the method to improve the insulation resistance is found. It was found that the surface bonding force between the metal soft magnetic powder and the coating layer increased first and then decreased with the increase of temperature, and the coating layer was brittle with the increase of temperature. The results show that the change of the volume change of the coating layer and the change of the surface binding force between the coating layer material in the curing process, and the higher the degree of curing the coating layer is brittle, and the interaction between the two and the coating layer can produce the peeling or even fall off. Keywords: Soft magnetic powder; Insulation resistance; Coated 一体成形电感用软磁粉末绝缘失效的研究 1 1 2 郭峰 ；李伟健 ；闫亮明 1：昆山磁通新材料科技有限公司 江苏省苏州市 中国 2：内蒙古工业大学 内蒙古呼和浩特市 中国 邮箱 bruce_guo@ （郭峰）；lwjv587@163.com （李伟健） （闫亮明） 摘要：本文主要研究一体成形电感用软磁粉末绝缘失效。实验主要探讨了一体成型电感在低温烘烤后绝缘阻抗突变的 原因，并试图找到改善绝缘阻抗的方法。通过研究发现金属软磁粉末及其包覆层之间的表面结合力随着温度升高先升 高后降低，且该包覆层物质随着温度的升高而脆化。研究结果证明绝缘阻抗突变的原因在于包覆层物质在固化过程中 的体积变化和固化产物引起表面结合力的变化，且固化程度越高包覆层越脆，二者相互作用后使得包覆层产生剥皮甚 至脱落，从而造成模压电感在烘烤后绝缘阻抗失效。 关键词：软磁粉末；绝缘阻抗；包覆 1.前言 软磁粉芯是由铁磁性粉末与绝缘介质混合并压制而成且具有分布式气隙的一种金属软磁材料，在此基础上将线圈 在成型前埋入粉末中并随后一起压制成型而成的器件叫做一体成型电感[1-3] （以下简称电感）。电感在电路中的基本 作用：滤波、振荡。在电子线路中，电感可以像导线一样通过直流电，但是对交流有限流作用，它与电阻器或电容器 能组成高通或低通滤波器、移相电路及谐振电路等。电感的