《甘蔗渣_NR复合材料的研究》-毕业设计（论文）.docVIP

PAGE 16 毕 业 论 文（设计） 摘 要 本文研究甘蔗渣/NR复合材料，通过对甘蔗渣进行预处理——碱处理法，使植物纤维中的部分果胶、木素和半纤维素等低分子杂质被溶解，纤维表面的杂质被除去，纤维表面变得粗糙，使界面之间黏合能力增强。然后分别用5份、10份、15份、20份、25份的甘蔗渣纤维改性NR，实验证明甘蔗渣纤维含量为10g、15g时获得了性能较好的复合材料。为了能获得优良的综合性能，对预处理的甘蔗渣纤维用不同浓度（0.5%、1%、1.5%、2%、2.5%、3%）的硅烷偶联剂再进行处理，实验证明浓度为2%硅烷偶联剂处理过的甘蔗渣纤维获得了更好的综合性能。 关键词 甘蔗渣纤维；NR；复合材料；碱处理；硅烷偶联剂  Abstract In this paper, bagasse / NR composites, bagasse by pretreatment - alkali treatment, so that some of the plant fiber pectin, lignin and hemicellulose was dissolved impurities such as low molecular weight, fiber surface impurities were removed fiber surface becomes rough, so that the interface between the bonding capacity. And then were treated with 5, 10, 15, 20, 25 copies of the modified bagasse fiber NR, experimental proof of bagasse fiber content of 10g, 15g performance was better when the composite material. In order to obtain good overall performance, the fiber bagasse pretreated with different concentrations (0.5%, 1%, 1.5%, 2%, 2.5%, 3%) of the silane coupling agent and then processing, experimental proof of the concentration of silane coupling agent of 2% treated bagasse fiber to obtain a better overall performance.Key words :bagasse fiber;NR;composite materials; alkali;silane coupling agent 目 录 TOC \o 1-3 \h \z \u 1 引言 4 2、实验部分 4 2.1 主要原材料及试剂 4 2.2 主要仪器 5 2.3 试验配方 5 2.4 试样的制备和测试 5 2.4.1 甘蔗渣纤维的预处理——碱处理法[ 5 2.4.1.1作用机理 5 2.4.1.2步骤 5 2.4.2甘蔗渣纤维的表面处理偶联法 6 2.4.2.1作用机理 6 2.4.2.2步骤 6 2.4.3 NR混炼胶的制备 6 2.5 性能测试 6 3、结果与分析 7 3.1碱处理对甘蔗/NR复合材料硫化特性的影响 7 3.2 碱处理对甘蔗渣/NR复合材料力学性能的影响 8 3.3硅烷偶联剂用量对甘蔗渣/NR复合材料硫化特性的影响 9 3.4硅烷偶联剂含量对甘蔗渣/NR的力学性能的影响 12 3.5碱处理与硅烷偶联剂处理复合材料力学性能的比较 13 4、结论 14 致 谢 16 参考文献 17 1 引言 复合材料是指把两种以上宏观上不同的材料，合理地进行复合而制得的一种材料，目的是通过复合来提高单一材料所不能发挥的各种特性。复合材料是多相材料。它包括基体相和增强相。基体相是一种连续相材料，它把改善性能的增强相材料固结成一体，并起传递应力的作用；增强相一般为分散相，主要起承受应力和显示功能的作用，这两相最终以复合材料的固相材料出现。复合材料既能保持原组成材料的重要特性，又可通过复合效应使各组分的性能相互补充，获得原组分不具备的许多优良性能。本文利