轻骨料透水混凝土的研究.docxVIP

南峰 1，金瑞灵 1，伍勇华 1，张建科 1，周新宇 2（1. 西安建筑科技 南 峰 1，金瑞灵 1，伍勇华 1，张建科 1，周新宇 2 （1. 西安建筑科技大学材料学院 710055；2. 上海唯中建材股份有限公司 200122) 摘 要：用粘土陶粒作为粗骨料、膨胀珍珠岩作为细骨料和其他胶凝材料（水泥和粉煤灰）通过人工搅拌的方法 配制轻骨料透水混凝土，研究不同的水泥、粉煤灰和细轻骨料用量对混凝土抗压强度、孔隙率、透水系数、pH 值及表 观密度等性能的影响。 结果表明，随着水泥、粉煤灰和细轻骨料用量的增加，轻骨料透水混凝土的强度增加、表观密 度增大，而孔隙率、透水系数会降低，pH 值变化不大。 关键词：透水混凝土；轻骨料；透水系数 Abstract: The lightweight aggregates pervious concrete is prepared by handing mixing, which is used by the ce- ramisite clay as coarse lightweight, the expand perlite as fine lightweight aggregates, fly ash and ordinary portland cement. The effects of various dosages of cement, fly ash and fine lightweight aggregates on the compressive strength, porosity, per- meability coefficient, pH value and apparent density of prepared concrete are researched. The results show that with the dosage increase of cement, fly ash and fine lightweight aggregates, strength and apparent density of concrete increase, but the porosity and permeability coefficient decrease, and the pH value changes a little. Key words：Pervious concrete; Lightweight aggregate; Permeability coefficient 中图分类号：TU528 文献标识码：A 文章编号：1000-4637（2012）03-22-04 0 前言 透水混凝土是用胶凝材 料与水拌合 后包裹特 定粒径的粗骨料而形成的多孔骨架结构。 因其具有 良好的透水透气性能， 而被用于路面和绿化， 具有 良好的经济效益和生态效益。 将轻骨料替代透水混 凝土中的碎石作为粗骨料而配制出的轻骨料透 水 混凝土， 与普通透水混凝土相比具有表观密度小、 质量轻、导热系数低等特点。 在其表面铺设一层薄 土种植草皮， 就可以用于护坡和道路绿化， 此类混 凝土也可以称为生态混凝土。 若对轻骨料透水混凝 土加以利用， 就可减轻环境负荷， 并对废弃物循环 利用，进而提高生态效益和经济效益。 我国对生态 混凝土的研究已有很多，主要是为了保护环境和提 高资源的利用[1~4]，但是我国对轻骨料混凝土的研究 是从上世纪 50 年代开始的 ， 到 90 年代， 陶粒 轻骨 料的应用进入一个全新时期[5]。 由于轻骨料的来源 比较广泛且成本较低 ， 如工业废料中的粉煤灰 陶 粒、粘土陶粒、膨胀矿渣珠等， 能够降低成本、 提高 材料的利用率。 掺入透水混凝土后，可大大降低透 水混凝土的自重和高成本，这对资源的利用和生态 平衡具有积极作用。 将粘土陶粒和膨胀珍珠岩作为粗细轻骨料，与 胶凝材料配制成轻骨料混凝土，通过分析各组分对 其性能的影响，即对抗压强度、透水系数、干表观密 度和 pH 值等性能的影响，找出影响规律，从而配制 出性能良好的轻骨料透水混凝土。 1 原材料 1.1 水泥 采用陕西秦岭某公司生产的 P·O42.5 级水泥， 其技术指标如表 1 所示。 表 1 水泥的技术性能指标 凝结时间/min 3d 强度/MPa 28d 强度/MPa 安定性 细度/% 初凝 终凝 抗折 抗压 抗折 抗压 合格 1.3 210 265 6.3 25.4 9.1 48.8 南 峰，金瑞灵，伍勇华，等轻骨料透水混凝土的研究粗骨 南 峰，金瑞灵，伍勇华，等 轻骨料透水混凝土的研究 粗骨料 采用陕西某公司生产的 粘土陶粒 ，