(第8章)钢的淬火与回火.ppt

Chapter 8 Quenching and Temping of Steel 8-63 Chapter 8 Quenching and Temping of Steel 8-64 ? 降低钢中杂质元素 ? 加入能细化A晶粒元素，如Nb、V、Ti ? 加入适量抑制二类回火脆性的元素：Mo、W ? 避开在450~650°C范围回火，650°C以上回火 要快冷。 Chapter 8 Quenching and Temping of Steel 8-65 8.5、钢的淬火/回火工艺制定 Chapter 8 Quenching and Temping of Steel 8-66 Chapter 8 Quenching and Temping of Steel 8-67 Chapter 8 Quenching and Temping of Steel 8-68 Chapter 6 Martensite and Its Transformation 6-63 8.5.2 回火工艺(温度)的制定 Chapter 8 Quenching and Temping of Steel 8-70 Chapter 8 Quenching and Temping of Steel 8-71 Chapter 8 Quenching and Temping of Steel 8-72 Chapter 8 Que