影响改进型高镍铬无限冷硬复合铸铁轧辊性能因素分析.docxVIP

影响改进型高镍铬无限冷硬复合铸铁轧辊性能因素分析 黄明，刘宇，肖连华 （唐山钢铁集团重机装备有限公司，河北 唐山 063000） 摘要：改进型高镍无限冷硬复合铸铁轧辊（以下简称改进型ICDP轧辊）轧辊组织由贝氏体、少量马氏体、残余奥氏体、渗碳体以及石墨等组成【1】，本文通过讨论成分变化制作工艺研究金相组织与性能之间的关系，分析出影响改进型ICDP轧辊性能的因素，以便于生产过程中有针对性的优化工艺，改进轧辊性能指标。 关键字：影响 改进型 ICDP轧辊 因素 Study on The Factors Affecting The Performance of Enhanced High NiCr Indefinnite Chilled Centrifugal Compound Cast Iron Roll Huang Ming，Liu Yu，Xiao Lian-hua （Tang Shan Iron and steel Group Heavy Machinery Equipment Co.Ltd.，Tangshan Hebei 063000，China） Abstract：Enhanced High NiCr Indefinnite Chilled Centrifugal Compound Cast Iron Roll(hereinafter referred to as the modified ICDP roll) roll tissue by bainite a small amount of residual austenite martensite cementite and graphite etc, this paper discussed composition changes in technology research of the relationship between microstructure and properties, analysis the influence factors of modified ICDP roll, so that the production process of targeted optimization process, enhance the roll performance index。 Key Words：Affecting，Enhanced，ICDP roll，index 改进型ICDP轧辊主要使用于热轧板带轧机，随着板材性能需求的提升，轧辊性能要求也越来越高，耐磨性、抗事故能力等；本文数据的建立是在唐山钢铁集团重机装备有限公司实验的基础上，通过不同成分的设计制作轧辊，并研究显微硬度、组织含量、耐磨粒子【2】分布等金相组织变化，了解组织与性能之间的关系。 1、组织性能分析 1.1显微硬度的测量 ICDP轧辊辊身基体组织为贝氏体+少量马氏体+残余奥氏体+渗碳体+石墨，为测定各个金相组织对轧辊总体硬度的影响，实验过程中在500×视场下对各个金相组织的显微硬度进行了测定，测定方式图片如图1所示： 图1 轧辊纤维硬度测定过程示意图 通过显微金相硬度的测定，我们可以得到表1所示的各个金相组织的显微硬度情况： 表1 各个金相组织的显微硬度情况 组织名称 维氏硬度 /HV 洛氏硬度 /HRC 肖氏硬度 /HSD 贝氏体+奥氏体 528 51.1 67.5 渗碳体 1144 太高无法转换 渗碳体+石墨 320 34 45.5 贝氏体 593 54.9 73.5 莱氏体 671 58.8 79.5 从显微硬度可以看出，渗碳体硬度最高，因此脆性也最大，与基体组织可以形成稳定的莱氏体结构，有利于基体的稳定；石墨硬度偏低，由于ICDP轧辊渗碳体含量较高，其主要作用是起到缓解轧辊裂纹倾向，但过多的石墨含量将降低轧辊性能。 1.2不同金相组织含量对轧辊性能的影响 Si元素为石墨析出元素，对轧辊组织石墨含量和渗碳体含量影响较大，通过现场实验当Si含量小于0.7%时，组织中石墨含量小于1%，轧辊抗裂纹能力低容易出现辊身裂纹、炸裂的现场，因此成分设定过程中选定Si含量0.7-0.9%，0.9-1.1%，1.1-1.3%三种成分进行测定。【3】 1.2.1石墨含量分析 通过金相实验，各Si含量ICDP轧辊石墨分布情况如图2所示，同时，通过电脑对金相图片的分析，得出各Si含量轧辊石墨的含量如表2所示： 表2 各Si含量ICDP轧辊石墨含量 % Si含量 1.1-1.3 0.9-1.1 0.7-0.9 石墨含量 5.22 3.4 1.7 a、Si含量1.1-1.3%石墨分布（100×） b、Si含