冷钢450m3级高炉操作制度探索 目录 TOC \o 1-9 \h \z \u 目录 1 正文 1 文1：冷钢450m3级高炉操作制度探索 1 SiO2 17 CaOiO2 17 文2：高炉自动化控制系统 20 1、系统设计 20 2、系统功能 21 3、系统特点 22 参考文摘引言： 23 原创性声明（模板） 24 文章致谢（模板） 24 正文 冷钢450m3级高炉操作制度探索 文1：冷钢450m3级高炉操作制度探索 Abstract Make an introduction of the four basic operation systems of 450m3 blast furnace in Lengshuijiang Iron and Steel Factory. (The four basic operation systems are forced draught blowing, loading, slag making and heat system.) Analyzed the common iide diameter gusty area not to adapt its special type of furnace; feeds the system to be also in develops the edge stage, the coal gas use factor is low, must realize ope the center, stable edge ; chooses the appropriate slag ingredient and the alkalinity, reduces the pig iron to contain the Si quantity is an important topic. Elaborated blast furnace four big operating dutys some principles and the adjustment method, cotructively proposed some coummate the operating duty, provides the itruction for the blast furnace operation, guaranteed that the blast furnace stabilizes along the line and strengthened smelting. Key Words blast furnace operation system 1 前言 冷钢450m3级高炉现有5座，1号2号3号高炉为450m3，4号5号高炉为530m3。采用串罐式无料钟炉顶布料系统；1、2、3、4号高炉为内燃式热风炉，5号高炉为卡鲁金顶燃式热风炉。其中1号高炉于2002年初开炉，到2007年11月28日五号高炉开炉。几年时间中，高炉利用系数一直在左右徘徊，且各高炉间生产不均衡，炉况很难长久稳定，炉况不顺时很难恢复，没有形成一套完善合理的操作制度。由于炉况不稳的影响，其它指标也很难上去。生铁含[Si]在%～%，焦比在450kg, 喷煤130kg, 高炉煤气CO2含量在11%～14%，风温在900～1150℃，与先进指标比差距很大。 先进高炉利用系数均值达到/m3#8226;d，新兴铸管芜湖公司2号高炉利用系数均值达到/m3#8226;d。先进的大型高炉生铁含[Si]在%～%，青钢、通钢、本钢一铁、新兴铸管等 企业 中小高炉生铁含[Si]在%左右。 生铁含[Si]每降低%可降低焦比4～5 kg。目前国内2000m3以上高炉入炉焦比先进水平是350kg，国外有的高炉达到了300kg以下。炼铁燃料比是入炉焦比+喷煤比，国际先进的燃料比小于500 kg，国际领先水平的燃料比是450kg左右。高炉燃料比低于500 kg的高炉煤气CO2含量均在21%以上，宝钢最高达24%。CO2含量升高%，炼铁燃料消耗降低10kg。 1999年9月宝钢1号高炉(4063m3)创造出月平均喷燥比 kg的最高纪录。2004年上半年宝钢1号高炉实现喷煤比206kg，2002年、2003年宝钢全公司高炉年平均喷煤比达到203kg的先进水平。控制好混合煤成分，实现煤焦置换比达到。实现高的煤气利用率(在50%左右)。合理的煤气流分布，最终实现高炉炼铁燃料比小于500kg。宝钢炼一吨铁的风耗是1100 m3，一些中型高炉是在1300m3风量，而大多数小高炉进行高冶炼强度操作，风耗在1500m3左右。 淮钢有两座 450m3高炉，于 2004 年 4