PAGE PAGE I PEA∕MDI∕EG体系TPU的制备及性能研究 摘要：本论文以聚己二酸乙二醇酯（PEA）为软段、4,4’-二苯基甲基异氰酸酯（MDI）和乙二醇（EG）为硬段，设计合理的实验配方合成热塑性聚氨酯弹性体(TPU)。采用旋转流变仪、拉力试验机、XRD衍射仪等手段研究TPU的流变性能、力学性能、结晶性等影响规律。结果表明，在相同长度的软段下，随着硬段含量的增大，其弹性模量和结晶性随之提高，断裂伸长率反而降低。在相同硬段含量，不同长度软段下合成的TPU，随着软段长度的增大，其动态性能有所差别。 关键词：热塑性聚氨酯弹性体，硬段含量，软段长度，力学性能，动态性能 Preparation and properties of PEA/MDI/EG system and TPU system Abstract: In this paper, polyethylene glycol adipate (PEA) as soft segments,4,4- twophenyl methyl isocyanate (MDI) and ethylene glycol (EG) as hard segment, the experimental formula and synthetic reasonable thermal design of thermoplastic polyurethane elastomer (TPU). Using a rotary rheometer, tensile testing machine, XRD diffraction methods to study TPU rheological properties, mechanical properties, crystallinity influences. The results show that, in the soft segment of the same length, with increasing hard segment content, the elastic modulus and crystallinity increased, the elongation at break decreases. In the same hard segment content, soft segments of different length synthesized TPU, with the increase of the length of the soft segment, which vary dynamic performance. Keywords: thermoplastic polyurethane elastomer, hard segment content, soft segment length, mechanics performance, dynamic performance 目 录 TOC \o 1-3 \h \u 27297 1 前言 1 9800 1.1聚氨酯的简介 1 19917 1.2 合成聚氨酯的原料 2 24958 1.2.1 聚合物多元醇 2 31389 1.2.2 异氰酸酯 2 6623 1.2.3 扩链剂 3 1704 1.3 聚氨酯弹性体 4 333 1.3.1 聚氨酯的合成机理 4 11344 1.3.2 聚氨酯弹性体的结构与性能 5 157 1.3.3 聚氨酯弹性体的发展趋势 7 20777 1.4 热塑性聚氨酯弹性体 8 20189 1.4.1 热塑性聚氨酯弹性体的概述 8 16550 1.4.2 热塑性聚氨酯弹性体的基本分类 9 17715 1.4.3 热塑性聚氨酯弹性体合成 9 27417 1.4.4 热塑性聚氨酯弹性体的应用开发 10 6640 2 实验部分 11 21549 2.1 实验原料 11 5978 2.2 实验仪器与设备 11 14107 2.3 TPU的制备 12 7986 2.3.1 TPU配方的计算 12 18250 2.3.2 制备TPU的配方 13 19092 2.3.3 合成TPU的工艺流程 14 14321 2.4 TPU的压片制样 15 3163 2.5 TPU的性能测试 15 29454 2.5.1 利用邵氏硬度仪测试TPU的硬度 15 9938 2.5.2 利用拉力试验机测试TPU的力学性能 15 22753 2.5.3 利用旋转流变仪测试TPU的流变性能 16 3026 2.5.4 利用XRD测试