反复熔铸对镍铬烤瓷合金硬度的影响.docVIP

反复熔铸对镍铬烤瓷合金硬度的影响 目录 TOC \o 1-9 \h \z \u 目录 1 正文 1 文1：反复熔铸对镍铬烤瓷合金硬度的影响 1 1 材料与方法 2 2 讨论 4 文2：反复熔铸对镍铬烤瓷合金硬度的影响 6 1 材料与方法 7 2 讨论 9 参考文摘引言： 10 原创性声明（模板） 11 文章致谢（模板） 11 正文 反复熔铸对镍铬烤瓷合金硬度的影响 文1：反复熔铸对镍铬烤瓷合金硬度的影响 ABSTRACT: Objective To study the effect of recasting on the hardness of the nickelchromium ceramic alloy. Methods The recast nickelchromium ceramic alloys were respectively obtained by recasting the nickelchromium alloy in pressure casting condition for once， twice， 3 times and 4 times. The recast alloys were respectively cast with uncast alloys (new alloys) to produce specime for hardness testing. The hardness specime were measured for Vicke hardness in a microhardness tester after initial grounding， resin inlay， and metallographic polishing. Results On the basis of their Vicke hardness， there was no significant difference between the alloys recast for 2～5 times and those cast for once(P). Conclusion The nickelchromium ceramic alloy can be recast for at least 5 times without impairing its hardness。 KEY WORDS: chromium alloys， nickel; metal ceramic alloys; dental casting technique; hardness 金瓷修复体制作过程中，为获得完整的烤瓷合金金属支架，投入铸造的合金常达到铸件自身所需合金量的2倍[1]；在铸造完成后，铸道、底座、储金球等附件常作为废弃物被丢弃，目前我国临床上使用最多的是镍铬合金金瓷修复体，由此产生大量镍铬烤瓷合金废旧料。因此，能否回收再利用烤瓷合金废弃物成为学者们关心的问题；而回收的烤瓷合金废弃物能否再利用取决于其各项性能指标。前期研究发现在真空加压氩气保护的铸造环境下，镍铬烤瓷合金经过5次熔铸，各主要元素组分的质量百分数和物相结构随着熔铸次数的增多未发生显著性变化；但随着熔铸次数增多其枝晶粗化，合金内部夹杂物和铸造缺陷增多；铸流率、弯曲性能、热膨胀系数、金瓷结合力、电化学腐蚀等无显著性变化[27]。力学性能指标之一硬度是表征固体材料抵抗弹性变形、塑性变形及破坏的能力。作为金瓷修复体金属支架的烤瓷合金在口腔咀嚼过程中受到多种外力的共同作用；因此，回收再利用的镍铬烤瓷合金废旧料的硬度值须符合临床要求。笔者从硬度角度研究反复熔铸对镍铬烤瓷合金的影响。 1 材料与方法 材料与设备 材料 硅橡胶印模材料（Rapid，瑞士Coltène/Whaledent公司）；铸造蜡（Mighty wax，日本SHOFU公司）；镍铬烤瓷合金（UNI METAL VH，日本SHOFU公司）；牙科镍铬磷酸盐铸造包埋材料（UNIVEST，日本SHOFU公司）；自凝树脂（中国上海医疗器械股份有限公司材料厂）；氧化铝耐水砂纸（钻石，中国上海砂轮厂）；三氧化二铬抛光粉（质量标准HG 393376，中国上海化学试剂公司） 设备 带吸尘器高速成切割机（RQY AG04， 美国Ray Foster公司）；真空铸造机（ARGONCASTERC，日本SHOFU公司）；笔式喷砂机（PenBlaster2，日本SHOFU公司）；粗喷砂机（JNCPⅡ型，中国天津嘉年公司）；金相试样抛光机（PG2D型，中国上海金相机械设备有限公司）；显微硬度计（HX1000，中国上海泰明光学