轴承钢夹杂物控制及精炼新工艺的研究.docx

轴承钢夹杂物控制及精炼新工艺的研究 摘要 轴承钢夹杂物不仅会降低产品的机械性能和使用寿命，同时也会对钢材表面质量、成形性和耐腐蚀性产生不利影响。因此，对轴承钢夹杂物控制和精炼新工艺进行研究具有重要意义。本文分析了轴承钢夹杂物的形成原因和种类，并介绍了夹杂物控制的方法和精炼工艺的发展历程。其中，通过引入先进的真空精炼技术和复合稀土元素的添加量和配比，可以有效地降低轴承钢中夹杂物的含量和尺寸，并提高钢材的性能和质量。最后，结合国内外相关研究成果，对轴承钢夹杂物控制和精炼新工艺的未来发展方向进行了探讨。 关键词：轴承钢；夹杂物；控制；精炼；新工艺 Abstract The inclusions in bearing steel will not only reduce the mechanical properties and service life of the product, but also have adverse effects on the surface quality, formability and corrosion resistance of the steel. Therefore, it is of great significance to study the control of inclusions in bearing steel and the new refining process. This paper analyzes the formation reasons and types of inclusions in bearing steel, and introduces the methods of inclusion control and the development process of refining process. Among them, by introducing advanced vacuum refining technology and adding and ratio of composite rare earth elements, the content and size of inclusions in bearing steel can be effectively reduced, and the performance and quality of steel can be improved. Finally, based on the relevant research results at home and abroad, the future development direction of inclusion control and refining new technology in bearing steel is discussed. Keywords: Bearing steel; Inclusions; Control; Refining; New technology 第一章 绪论 1.1 研究背景 轴承作为机械领域中最为常见的基本零件之一，其在汽车、机械、航空等众多领域都有广泛的应用。而轴承制造中所用的轴承钢，其性能和质量的优劣直接影响着轴承产品的可靠性、精确度和寿命等方面。其中，轴承钢中夹杂物作为一种具有明显负面影响的重要缺陷之一，已成为目前轴承钢研究领域中的热点和难点问题。 夹杂物是指有害性质的非金属包括物，是几乎所有金属材料中普遍存在的缺陷之一。夹杂物在轴承钢中的主要成分为氧化物、硫化物、氮化物、碳化物等。这些夹杂物会影响轴... 未完，完整内容请下载查看！